Journal of Nanomaterials
Volume 2015 (2015), Article ID 580582, 10 pages
http://dx.doi.org/10.1155/2015/580582

Research Article

Effect of Pr, Sm, and Tb Doping on the Morphology, Crystallite Size, and N₂O Decomposition Activity of Co₃O₄ Nanorods

Bahaa M. Abu-Zied,¹ Salem M. Bawaked,² Samia A. Kosa,² and Wilhelm Schwieger³

¹Center of Excellence for Advanced Materials Research (CEAMR), King Abdulaziz University, P.O. Box 80203, Jeddah 21589, Saudi Arabia
²Chemistry Department, Faculty of Science, King Abdulaziz University, P.O. Box 80203, Jeddah 21589, Saudi Arabia
³Institut für Chemische Reaktionstechnik, Friedrich-Alexander-Universität Erlangen-Nürnberg, Egerlandstraße 3, 91058 Erlangen, Germany

Received 5 September 2015; Accepted 17 November 2015

Academic Editor: John Zhanhu Guo

Copyright © 2015 Bahaa M. Abu-Zied et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

Cobalt(II,III) oxide, Co₃O₄, is a promising catalyst for nitrous oxide direct decomposition. In this paper we report effect of doping with some rare earth (RE) elements (Pr, Sm, and Tb) on the morphology and crystallite size of Co₃O₄ nanorods. The various precursors (RE/Co oxalates) were prepared via the microwave assisted method and subsequent calcination. The decomposition pathway of these precursors was followed using thermogravimetric analysis (TGA). Based on thermal analysis results, Pr-, Sm-, and Tb-doped Co₃O₄ samples were obtained via the calcination in static air at 500°C for their oxalate precursors. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and hydrogen temperature programmed reduction (H₂-TPR) were used to characterize the RE-doped cobalt oxide catalysts. The activity of the prepared catalysts was investigated for N₂O direct decomposition and compared with that of the undoped Co₃O₄ catalyst. It was shown that the promoted Co₃O₄ catalysts revealed higher activity compared to the unpromoted one. The dependence of the activity on both the catalysts particle size and the reduction behaviour was discussed.

1. Introduction

Due to the unawareness of its harmful effects nitrous oxide (N₂O) has suffered, for a long time, from the lack of interest from the environmental scientists [1, 2]. Only during the last two decades a growing interest can be noticed with N₂O abetment studies. This is especially after its citation as a second, non-CO₂ greenhouse gas. Moreover, it was recognized that it causes the destruction of ozone in the stratosphere and it causes the acid rains. Due to its long lifetime, about 150 years, N₂O has a Global Warming Potential (GWP) of 310 and 21 times that of CO₂ and CH₄, respectively [1, 2]. The industrial processes that involve N₂O emission include adipic acid, nitric acid, caprolactam, acrylonitrile, and glyoxal manufactures. Moreover, N₂O is emitted as a byproduct of some processes like the nonselective catalytic reduction of NO (NSCR) with cyanuric acid or urea and in three-way catalysis (TWC) to remove NO, CO, and hydrocarbons [1, 2].

Accordingly, N₂O was cited as the second non-CO₂ greenhouse gas Kyoto Protocol of the United Nations Convention on Climate Change (December 1997). Based on that protocol the industrial countries should reduce their collective greenhouse gas (GHG) emissions by values slightly higher than 5% below their 1990 values [1, 2]. On the other hand, the developed countries have to reduce their GHG emissions by values of around 5%. Such targets will be increased in the next protocol of the United Nations that will replace the Kyoto protocol. The catalytic routes represent the most important and applied solutions for this environmental problem. Among them the direct decomposition of nitrous oxide to its elements, that is, nitrogen and oxygen, is considered to be a simple and effective way to minimize the N₂O emissions. Many catalysts categories have been developed for N₂O decomposition.

Cobalt(II,III) oxide, Co₃O₄, is a black antiferromagnetic solid, p-type semiconductor and has direct optical band gap at 2.18–3.52 eV [3]. Co₃O₄ adopts the normal spinel structure, represented as AB₂O₄ in which A ions, Co²⁺(3d⁷), occupying tetrahedral sites and B ions, Co³⁺(3d⁶), are located in octahedral sites. Co₃O₄ has been investigated extensively as promising catalysts for N₂O direct decomposition [4–14].

Russo et al. [4] have checked the activity of three series of metal (Mg, Ca, Mn, Co, Ni, Cu, Cr, Fe, and Z) spinels (cobaltites, chromites, and ferrites) prepared by the solution combustion method. Their results demonstrated that among the categories the cobalt containing spinels exhibit the best activity. Moreover, MgCo₂O₄ showed the best performance among the different metal cobaltites in the absence and presence of oxygen. This was attributed to its higher concentration of suprafacial-weakly chemisorbed oxygen species. Over a series of (M = Mg, Ni, Zn, ) spinel catalysts, prepared by the coprecipitation method, Yan et al. [5, 6] found that the N₂O decomposition activity depends on the degree of Co²⁺ substitution by Mg²⁺ or Ni²⁺ or Zn²⁺. The highest activities were observed over Mg0.54Co0.46Co₂O₄, Ni0.74Co0.26Co₂O₄, and Zn0.36Co0.64Co₂O₄ catalysts. Concurrently, for and () spinel-oxide catalysts, prepared via the coprecipitation method, it was found that the highest activity was exhibited by the catalysts 0.75 and 0.50, respectively [7, 8]. Moreover, increasing the calcination temperature till 900°C for both series was accompanied by a sharp activity decrease. The activity of () catalysts, prepared by the impregnation method, was found to increase the -value [9].

With respect to the influence of promoters, Xue et al. reported a beneficial effect on doping Co₃O₄ spinel with ceria [10]. On varying the Ce/Co molar ratio, a complete N₂O conversion below 400°C was obtained for the catalyst having a ratio of 0.05. The promotion effect was attributed to the role of CeO₂ in promoting the reduction of Co³⁺ to Co²⁺, thus facilitating the desorption of adsorbed oxygen species, which is deemed to be the rate-determining step for N₂O decomposition. The activity of cobalt containing spinels was also markedly enhanced by doping with alkali cations. In this regard, the presence of residual K ions has led to an activity enhancement for Co₃O₄-CeO₂ (Ce/Co = 0.05) catalyst [11]. Potassium and cesium ions were found to be superior to lithium and sodium ones [9]. Recently, an activity enhancement was reported by the addition of K ions to Zn0.4Co2.6O₄ [12], MgCo₂O₄ [9], and Co₃O₄ [13] catalysts. Doping with alkali earth cations was also reported to improve the activity of spinel oxide catalysts. In this context, N₂O decomposition over a series of MCO₃-Co₃O₄ (M = Ca, Sr, Ba) catalysts having M/Co ratios of 0.1–0.4 revealed that the catalysts containing Sr and Ba ions exhibit the highest activity [14]. The crystallite size and the calcination temperature are other factors that influence the N₂O decomposition of the oxide spinel catalysts; lower values of both factors increase the catalytic activity [7–9, 14].

The previous literature data reveals that the activity of Co₃O₄ spinel oxide-based catalysts is sensitive to the preparation method, the degree of Co²⁺ substitution, the calcination temperature, crystallite size, and presence of dopants. The role of rare earth oxides as promoters during N₂O direct decomposition was reported for some catalytic systems. For instance, Bueno-López et al. [15] demonstrated that the addition of La, Pr dopants increases the activity of Rh/CeO₂ catalysts markedly. This was attributed to the role of the added RE cation in stabilizing the catalysts active phase (Rh₂O₃). Synergic catalytic performance compared to the single oxides was reported for CuO/CeO₂ catalysts [16]. This effect was related to the enhanced catalysts reducibility as well as the facile Ce⁴⁺/Ce³⁺ and Cu²⁺/Cu⁺ redox cycles. Concurrently, Konsolakis et al. [17] reported a dramatic enhancement of de-N₂O performance of Pt/Al₂O₃ by the incorporation of 20 wt% CeO₂-La₂O₃ mixed oxide on the Al₂O₃ support. To the best of our knowledge, there are limited reports concerning the influence of the rare earth oxides dopants on the N₂O decomposition activity of Co₃O₄ spinel oxide catalyst. Therefore, based on the expected promotion effect of the RE dopants as it was reported for other catalysts, in this paper we report the enhancement effect of doping Co₃O₄ nanorods with some rare earth (RE) elements (Pr, Sm, and Tb) during N₂O direct decomposition. The examined catalysts were prepared via the microwave assisted method of cobalt oxalate and subsequent calcination. Special focus will be given to the catalysts characterization in order to check the influence of the added RE elements on the morphology and crystallite size of Co₃O₄ nanorods.

2. Materials and Methods

2.1. Catalysts Preparation

Cobalt nitrate (Co(NO₃)₂·6H₂O), praseodymium nitrate (Pr(NO₃)₃·6H₂O), samarium nitrate (Sm(NO₃)₃·6H₂O), terbium nitrate (Tb(NO₃)₃·6H₂O), oxalic acid (H₂C₂O₄), and cetyltrimethylammonium bromide (CTAB) are of analytical grade and were used as received without further purification. Co₃O₄ was prepared by microwave assisted precipitation method (in the form of cobalt oxalate) using a microwave power of 560 W and subsequent calcination at 500°C. Detailed information about the preparation procedure is given elsewhere [18]. The rare earth-promoted Co₃O₄ catalysts were prepared employing the coprecipitation method. In this method the amount of a rare earth cation (Pr³⁺, Sm³⁺, and Tb³⁺), required to achieve rare earth (RE)/Co ratio of 0.05, was added during the precipitation of cobalt oxalate using the same working procedure. After drying the coprecipitated oxalates, they were calcined for 1 h at 500°C in air to yield the corresponding earth-promoted Co₃O₄ catalysts. Scheme 1 shows an illustration and mechanism of the Co₃O₄ and RE/Co₃O₄ catalyst synthesis.

Scheme 1: A schematic illustration and mechanism of the Co₃O₄ and RE/Co₃O₄ catalyst synthesis.

2.2. Characterization Techniques

TGA and DTG curves were recorded with the aid of TA instrument apparatus (model TGA-Q500) using a heating rate of 10°C min⁻¹ and an average sample weight of 5 mg in nitrogen flow (40 mL min⁻¹). X-ray powder diffraction (XRD) patterns were performed for the prepared RE/Co₃O₄ catalysts using a computerized Philips diffractometer (type PW 103/00) operated with Cu Kα radiation (λ = 1.5405 Å) at 35 kV and 20 mA. The step scans were taken over the 2θ range of 4–80° in a step of 0.06 min⁻¹. FT-IR spectra were performed over the wavenumber range of 4000–400 cm⁻¹ using Attenuated Total Reflectance (ATR) sampling accessory on the Nicolet iS50 FT-IR spectrometer. Catalysts morphologies were characterized by scanning electron microscopy (JEOL-JSM-5400 LV). Prior to the SEM observations the catalysts were sputter with gold. Transmission electron microscopy (TEM) images were performed using JEOL (model JEM-1011) microscopy. Hydrogen temperature-programmed reduction (H₂-TPR) experiments were performed on Quantachrome CHEMBET-3000 instrument.

2.3. Activity Measurements

The catalytic tests were carried out in a fixed-bed quartz-glass flow reactor, at atmospheric pressure, containing approximately 0.5 g of the catalyst. The experiments were carried out at the temperature range of 150–500°C and a W/F value of 0.15 g s cm⁻³. The N₂O gas was introduced onto the catalyst bed from the bottom. The reactor was heated using a temperature-controlled furnace. The temperature in the reactor was measured using a thermocouple on the catalyst bed. Prior to the reaction all the catalysts were pretreated for 1 h in helium at 500°C. The reactant gas, 500 ppm N₂O, was introduced to the catalyst bed with the aid of Bronkhorst thermal mass flow controllers using helium as a balance gas. The N₂O concentrations in the inlet and outlet streams were measured using nondispersive infrared analyser (Hartmann and Braun, Uras 10E).

3. Results and Discussion

3.1. Catalysts Characterization

As it was mentioned in the introduction that the calcination temperature has a crucial effect on the catalytic behaviour of the Co₃O₄-based catalysts, therefore, in order to identify the appropriate calcination temperature of the parent cobalt oxalate and its RE-containing mixtures, the thermal stability of these parents has been checked by TGA during the heating up to 700°C. Our more recent work demonstrated that the preparation procedure followed has led to the formation of cobalt oxalate with the formula CoC₂O₄·2H₂O [18]. The obtained TGA-DTG curves are shown in Figure 1. Two weight loss (WL) events can be observed for the undoped cobalt oxalate (Figure 1(a)). These events are accompanied by WL values of 19.58 and 46.11% and are maximized at 162 and 366°C. The first WL agrees well with that (19.69%) expected for the dehydration of the parent CoC₂O₄·2H₂O. The obtained second WL% is higher than that expected for the formation of Co₃O₄ (36.44%) or CoO (39.36%) and lower than that anticipated for the formation of metallic Co (48.10%). This suggests that the residue formed in the second step is composed mainly of metallic cobalt. In agreement, Deng et al. [19] reported the formation of β-Co as a result of the thermal decomposition of its β-CoC₂O₄·2H₂O precursor in N₂ flow at 395°C. In this context, it is to be mentioned that conducting the experiment air flow has led to the formation of Co₃O₄ as a second decomposition step product [18–20]. The TGA thermograms obtained for the RE/cobalt oxalate mixtures (Figures 1(b)–1(d)) reveal the emergence of an early WL step (maximized at the temperature range of 54–86°C). This step could be related to the dehydration of the RE oxalates. Meanwhile, two other peaks can be observed in the three thermograms, which are maximized at the temperature ranges of 162–170°C and 366–372°C. No other WL steps can be observed in the three thermograms. Therefore, it is plausible to assign the former set of peaks to the dehydration of cobalt oxalate, whereas the second set of peaks is assigned to the decomposition of the anhydrous RE/cobalt oxalates. TGA curve of the Tb/Co mixture indicates the presence of a mild-gradual weight gain at temperatures higher than 425°C. This weight gain could be related to the oxidation of the obtained metallic cobalt by the traced amount of oxygen in the flow. According to the TGA results the various parents were calcined at 500°C for 1 h in order to obtain the relevant nanocrystalline Co₃O₄-based catalysts.

(a)

(b)

(c)

(d)

Figure 1: TGA-DTG curves obtained by heating the dried undoped cobalt oxalate (a), praseodymium/cobalt oxalates (b), samarium/cobalt oxalates (c), and terbium/cobalt (d) oxalates till 700°C.

Figure 2 shows the XRD patterns of the calcined cobalt oxalate and its RE-containing mixtures. XRD pattern for the undoped Co₃O₄ catalyst (Figure 2(a)) reveals that the presence of reflections matches well with those of the cubic Co₃O₄ spinel oxide (space group Fd3m; JCPDS card number 42-1467) [18, 20–26]. No other peaks assignable to Co₂O₃, CoO, and Co were detected indicating that the decomposition of cobalt oxalate in air proceeds with the formation of Co₃O₄ spinel oxide as a pure phase. The XRD pattern of the Pr containing catalyst (Figure 2(b)) reveals the presence of reflections due to the Co₃O₄ spinel oxide together with very small intensity ones at 2θ = 28.38°, 33.07°, and 47.02°. These reflections could be ascribed to the presence of Pr₆O₁₁ phase (JCPDS card number 42-1121). This indicates that this catalyst is composed of Co₃O₄ as a major phase together with trace amount of Pr₆O₁₁. The diffractogram of the Sm/Co catalyst (Figure 2(c)) shows the existence of high-intensity peaks characterizing the Co₃O₄ spinel together with two weak reflections at 2θ = 28.38° and 47.12°. These two reflections could be assigned to the Sm₂O₃ phase (JCPDS card number 76-0153). This, in turn, suggests the coexistence of Co₃O₄ (major) and Sm₂O₃ (trace) for this sample. Finally, the XRD pattern of the Tb/Co catalyst (Figure 2(d)) reveals the presence of all the peaks due the Co₃O₄ spinel as a major phase. In addition, two small reflections emerged at 2θ = 42.44° and 61.52°, which can be assigned to CoO phase (JCPDS card number 78-0431). Moreover, two other weak-intensity peaks appear at 2θ = 29.06° and 48.69°, which indicates the presence of trace amount of Tb₄O₇ (JCPDS card number 13-0387).

Figure 2: XRD patterns of Co₃O₄ (a) catalyst and its Pr (b), Sm (c), and Tb (d) containing catalysts being prepared by the impregnation method at RE/Co ratio of 0.05 and calcined at 500°C.

The FT-IR spectra of the calcined cobalt oxalate and its RE-containing mixtures are shown in Figure 3. For all samples, FTIR spectra revealed the presence of two absorptions located at 560–567 and 656–670 cm⁻¹. These two absorptions can be assigned, respectively, to ν ₁ and ν ₂ stretching vibrations of the metal-oxygen bond in Co₃O₄ [3, 14, 18, 25–27]. The RE oxide containing catalysts reveals the presence of other weak absorptions at the wavenumber range of 1700–1200 cm⁻¹, which can be assigned to the presence of surface carbonate species [7, 8, 14]. This indicates the ability of the added RE oxides to form weak surface carbonates upon contact with atmospheric air.

Figure 3: FTIR spectra of Co₃O₄ (a) catalyst and its Pr (b), Sm (c), and Tb (d) containing catalysts being prepared by the impregnation method at RE/Co ratio of 0.05 and calcined at 500°C.

Figure 4 shows the SEM images of the neat Co₃O₄ as well as its Pr, Sm, and Tb containing catalysts prepared by the coprecipitation method and calcined at 500°C. It is evident that the neat Co₃O₄ (Figure 4(a)) consists of sets of rods. Adding the RE oxides to Co₃O₄ resulted in dramatic morphological changes. The Pr₆O₁₁/Co₃O₄ catalyst (Figure 4(b)) consists of network polygons within the frame of spheres agglomerations. The Sm₂O₃/Co₃O₄ (Figure 4(c)) consists of sets of welded rods which have smaller dimensions than those of the neat Co₃O₄. Finally, the Tb₄O₇/Co₃O₄ catalyst (Figure 4(d)) shows agglomeration of polydisperse rectangles.

(a)

(b)

(c)

(d)

Figure 4: SEM images of as-prepared Co₃O₄ (a), Pr₆O₁₁/Co₃O₄ (b), Sm₂O₃/Co₃O₄ (c), and Tb₄O₇/Co₃O₄ (d) being prepared by the coprecipitation method and calcined at 500°C.

The TEM images of the neat Co₃O₄ as well as its Pr, Sm, and Tb containing catalysts prepared by the coprecipitation method and calcined at 500°C are depicted in Figure 5. One can clearly show that rod morphology of the unpromoted Co₃O₄ (Figure 5(a)) is composed of sets of capsules having diameters in the range of 35–65 nm and lengths of 50–180 nm. These rods are welded to form larger ones. The Pr₆O₁₁/Co₃O₄ catalyst (Figure 5(b)) shows irregular shape particles having diameters in the range of 15–50 nm. Similar morphology can be seen for the Sm₂O₃/Co₃O₄ catalyst (Figure 5(c)) with particles diameters in the range of 20–60 nm. The Tb₄O₇/Co₃O₄ catalyst (Figure 5(d)) shows irregular shaped agglomerations of particles with dimensions in the range of 20–100 nm. Thus, the electron microscopic examination reveals that the rod-like morphology of Co₃O₄ is very sensitive to the presence of these RE oxides. The presence of such dopants even in small concentration is sufficient to destroy this rod-like morphology.

(a)

(b)

(c)

(d)

Figure 5: TEM images of as-prepared Co₃O₄ (a), Pr₆O₁₁/Co₃O₄ (b), Sm₂O₃/Co₃O₄ (c), and Tb₄O₇/Co₃O₄ (d) being prepared by the coprecipitation method and calcined at 500°C.

3.2. Catalytic Activity Measurements

The activity of the three RE-promoted Co₃O₄ catalysts was tested for N₂O decomposition and compared with that of the unpromoted Co₃O₄. Figure 6 shows the dependence of N₂O conversion percentage on the reactor temperature for these series of catalysts being prepared by the coprecipitation method. One can easily spot the fact that the activity increases continuously with the reactor temperature over all the tested catalysts. Moreover, all the RE containing catalysts showed higher N₂O decomposition activity compared to the bare Co₃O₄ catalyst. In the open literature, there are many papers reporting the promotion effect of various promoters during N₂O decomposition over Co₃O₄-based catalysts. For instance, partial substitution of Co²⁺ ions in Co₃O₄ spinel oxide with various metal ions (Mg²⁺, Ni²⁺, Cu²⁺, and Zn²⁺) has led to a noticeable increasing of its activity [5–9]. Activity enhancement was observed also on doping Co₃O₄-based catalysts with some promoters like ceria [10], zirconia [28], alkali [11–13, 29, 30], and alkali-earth [14] cations. In some of these papers the enhanced N₂O decomposition activity was correlated with the Co₃O₄ crystallite size [7–9, 14], where high activity was observed over small Co₃O₄ crystallite size. Concurrently, an inverse relationship between the Ag⁰ crystallites size and the N₂O conversion % was reported for catalysts [31]. Similarly, the higher N₂O decomposition activity of the RE/Co₃O₄ catalysts compared to that of the bare Co₃O₄ one could be related to the induced Co₃O₄ crystallite size reduction by the added RE ions as it was observed during the TEM analysis (Figure 5).

Figure 6: Dependence of N₂O conversion % on the reaction temperature of the Co₃O₄, Pr₆O₁₁/Co₃O₄, Sm₂O₃/Co₃O₄, and Tb₄O₇/Co₃O₄ catalysts.

The reported reaction mechanism of the N₂O decomposition over Co₃O₄-based catalysts involves electron donation from an active center at the catalyst surface, which is a metal ion in a low oxidation state (probably Co²⁺), to the N₂O molecule as follows [9, 14, 28]:

This step is accompanied by Co²⁺ oxidation to Co³⁺ together with the formation of one N₂ molecule and a chemisorbed oxygen atom. Thus, the recoverability of Co²⁺ is crucial for attaining high N₂O decomposition activity as shown in (3). One has

Therefore, H₂-TPR measurements were performed in order to examine the effect of the addition of RE ions on the reduction behaviour of Co₃O₄ spinel oxide. The obtained TPR curves of these catalysts are depicted in Figure 7. All the TPR profiles in Figure 7 reveal the existence of one broad peak, which extends over the temperature range of 280–520°C. This finding indicates that this peak could describe several overlapping reduction processes. In agreement with other literature data, such peak could be assigned to the reduction of Co³⁺ to Co²⁺ and Co²⁺ to Co⁰ according to [10, 32]:

Figure 7: Comparison of H₂-TPR profiles of undoped Co₃O₄ and its Pr-, Sm-, and Tb-doped catalysts.

The obtained TPR profiles indicate that the reduction behaviour of Co₃O₄ is greatly influenced by the added RE oxides. of the reduction peak is shifted from 448°C for Co₃O₄ to 441, 435, and 431°C for Pr-, Sm-, and Tb-promoted Co₃O₄, respectively. Moreover, the onset temperature of the reduction is shifted towards lower temperatures for the RE-promoted Co₃O₄ compared to the unpromoted one. These findings, in turn, suggest that the reduction behaviour of Co₃O₄ is enhanced by the addition of the RE oxides.

More recently, it was demonstrated that the fine tuning of Cu facilitates the reduction of Co³⁺ and Co²⁺ in spinel [33]. This promotion of the catalysts reducibility was correlated with the increase in the N₂O direct decomposition over this series of catalysts. For a series of Ce-doped Co₃O₄ catalysts, Xue et al. [10, 11] showed that the reduction behaviour of these catalysts is influenced by the Ce/Co ratio as well as the preparation method. They concluded that the higher the Co³⁺ reducibility of the Co₃O₄-CeO₂ catalyst, the higher the N₂O decomposition activity. Chromčáková et al. [32] reported a direct dependence of the reduction ability and the catalytic behaviour during N₂O direct decomposition of a series of Co₃O₄ catalysts prepared via different routes. The results of N₂O decomposition over bare Pr₆O₁₁, Sm₂O₃, and Tb₄O₇ (not shown) revealed that these oxides exhibit very low activities (less than 5% conversion at 500°C). This finding suggests that the active catalysts centers could be Co²⁺-Co³⁺ redox pair. And based on the H₂-TPR results, we can confidently state that the improved reducibility of the Co³⁺ to Co²⁺, induced by the incorporation of RE oxides into Co₃O₄, could be an additional factor for their higher N₂O decomposition activity compared to that of the unpromoted Co₃O₄. Accordingly, the reaction mechanism can be understood as follows: as the reaction proceeds N₂O is adsorbed on an active catalyst center (Co²⁺) as indicated by (1). This step is followed by the liberation of one nitrogen molecule leaving back and adsorbed oxygen atom over a catalyst center with higher oxidation state, that is, Co³⁺. The addition of the RE oxides to improve the reducibility of the catalyst, that is, enhances the recoverability of the catalyst active center (Co²⁺) as indicated by (3).

4. Conclusions

Series of RE-doped Co₃O₄ precursors were prepared by the microwave assisted method employing oxalic acid as precipitating agent. The RE-doped Co₃O₄ catalysts were obtained by the calcination, in air at 500°C, of these precursors. The obtained catalysts were characterized using XRD, FT-IR, SEM, TEM, and H₂-TPR techniques and tested for N₂O direct decomposition. It was found that the addition of the RE oxides to the Co₃O₄ spinel enhances its N₂O decomposition activity. The superior activity of the RE-promoted Co₃O₄ catalysts to that of the unpromoted Co₃O₄ one was correlated with the observed decrease in the particle size of Co₃O₄ as well as the facilitated Co³⁺ → Co²⁺ reduction.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This project was supported by the National Science, Technology and Innovation Plan (MAARIFAH) strategic technologies programs, no. 12-ENV2756-03, of the Kingdom of Saudi Arabia. The authors thankfully acknowledge Science and Technology Unit, Deanship of Scientific Research at King Abdulaziz University, for their technical support.

References

J. Pérez-Ramírez, “Prospects of N₂O emission regulations in the European fertilizer industry,” Applied Catalysis B: Environmental, vol. 70, no. 1–4, pp. 31–35, 2007.

J. Pérez-Ramírez, F. Kapteijn, K. Schöffel, and J. A. Moulijn, “Formation and control of N₂O in nitric acid production: where do we stand today?” Applied Catalysis B: Environmental, vol. 44, no. 2, pp. 117–151, 2003.

M. T. Makhlouf, B. M. Abu-Zied, and T. H. Mansoure, “Effect of calcination temperature on the H₂O₂ decomposition activity of nano-crystalline Co₃O₄ prepared by combustion method,” Applied Surface Science, vol. 274, pp. 45–52, 2013.

N. Russo, D. Fino, G. Saracco, and V. Specchia, “N₂O catalytic decomposition over various spinel-type oxides,” Catalysis Today, vol. 119, no. 1–4, pp. 228–232, 2007.

L. Yan, T. Ren, X. Wang, D. Ji, and J. Suo, “Catalytic decomposition of N₂O over MxCo1−xCo₂O₄ (M = Ni, Mg) spinel oxides,” Applied Catalysis B: Environmental, vol. 45, no. 2, pp. 85–90, 2003.

L. Yan, T. Ren, X. Wang, Q. Gao, D. Ji, and J. Suo, “Excellent catalytic performance of spinel catalysts for the decomposition of nitrous oxide,” Catalysis Communications, vol. 4, no. 10, pp. 505–509, 2003.

B. M. Abu-Zied, S. A. Soliman, and S. E. Abdellah, “Enhanced direct N₂O decomposition over CuxCo1−xCo₂O₄ (0.0 ≤ x ≤ 1.0) spinel-oxide catalysts,” Journal of Industrial and Engineering Chemistry, vol. 21, pp. 814–821, 2015.

B. M. Abu-Zied, S. A. Soliman, and S. E. Abdellah, “Pure and Ni-substituted Co₃O₄ spinel catalysts for direct N₂O decomposition,” Chinese Journal of Catalysis, vol. 35, no. 7, pp. 1105–1112, 2014.

B. M. Abu-Zied, “Nitrous oxide decomposition over alkali-promoted magnesium cobaltite catalysts,” Chinese Journal of Catalysis, vol. 32, no. 1-2, pp. 264–272, 2011.

L. Xue, C. Zhang, H. He, and Y. Teraoka, “Catalytic decomposition of N₂O over CeO₂ promoted Co₃O₄ spinel catalyst,” Applied Catalysis B: Environmental, vol. 75, no. 3-4, pp. 167–174, 2007.

L. Xue, C. Zhang, H. He, and Y. Teraoka, “Promotion effect of residual K on the decomposition of N₂O over cobalt-cerium mixed oxide catalyst,” Catalysis Today, vol. 126, no. 3-4, pp. 449–455, 2007.

P. Stelmachowski, F. Zasada, G. Maniak et al., “Optimization of multicomponent cobalt spinel catalyst for N₂O abatement from nitric acid plant tail gases: laboratory and pilot plant studies,” Catalysis Letters, vol. 130, no. 3-4, pp. 637–641, 2009.

C. Ohnishi, K. Asano, S. Iwamoto, K. Chikama, and M. Inoue, “Alkali-doped Co₃O₄ catalysts for direct decomposition of N₂O in the presence of oxygen,” Catalysis Today, vol. 120, no. 2, pp. 145–150, 2007.

B. M. Abu-Zied and S. A. Soliman, “Nitrous oxide decomposition over MCO₃–Co₃O₄ (M = Ca, Sr, Ba) catalysts,” Catalysis Letters, vol. 132, no. 3-4, pp. 299–310, 2009.

A. Bueno-López, I. Such-Basáñez, and C. Salinas-Martínez de Lecea, “Stabilization of active Rh₂O₃ species for catalytic decomposition of N₂O on La-, Pr-doped CeO₂,” Journal of Catalysis, vol. 244, no. 1, pp. 102–112, 2006.

M. Konsolakis, S. A. C. Carabineiro, E. Papista et al., “Effect of preparation method on the solid state properties and the deN₂O performance of CuO–CeO₂ oxides,” Catalysis Science & Technology, vol. 5, no. 7, pp. 3714–3727, 2015.

M. Konsolakis, F. Aligizou, G. Goula, and I. Yentekakis, “N₂O decomposition over doubly-promoted Pt(K)/Al₂O₃–(CeO₂–La₂O₃) structured catalysts: on the combined effects of promotion and feed composition,” Chemical Engineering Journal, vol. 230, pp. 286–295, 2013.

B. M. Abu-Zied, S. M. Bawaked, S. A. Kosa, and W. Schwieger, “Effect of microwave power on the thermal genesis of Co₃O₄ nanoparticles from cobalt oxalate micro-rods,” Applied Surface Science, vol. 351, pp. 600–609, 2015.

Y. Deng, X. Xiong, J. P. Zou, L. Deng, and M. J. Tu, “Control of morphology and structure for β-Co nanoparticles from cobalt oxalate and research on its phase-change mechanism,” Journal of Alloys and Compounds, vol. 618, pp. 497–503, 2015.

L.-N. Jin, J.-G. Wang, X.-Y. Qian, D. Xia, and M.-D. Dong, “Catalytic activity of Co₃O₄ nanomaterials with different morphologies for the thermal decomposition of ammonium perchlorate,” Journal of Nanomaterials, vol. 2015, Article ID 854310, 7 pages, 2015.

H. Xu, Z. Hai, J. Diwu et al., “Synthesis and microwave absorption properties of core-shell structured Co₃O₄-PANI nanocomposites,” Journal of Nanomaterials, vol. 2015, Article ID 845983, 8 pages, 2015.

M. Rashad, M. Rüsing, G. Berth, K. Lischka, and A. Pawlis, “CuO and Co₃O₄ nanoparticles: synthesis, characterizations, and raman spectroscopy,” Journal of Nanomaterials, vol. 2013, Article ID 714853, 6 pages, 2013.

J. Jiang, F. Wei, G. Yu, and Y. Sui, “Co₃O₄ electrode prepared by using metal-organic framework as a host for supercapacitors,” Journal of Nanomaterials, vol. 2015, Article ID 192174, 6 pages, 2015.

L. Gao, J. Diwu, Q. Zhang et al., “A green and facile Synthesis of carbon-incorporated Co₃O₄ nanoparticles and their photocatalytic activity for hydrogen evolution,” Journal of Nanomaterials, vol. 2015, Article ID 618492, 7 pages, 2015.

M. T. Makhlouf, B. M. Abu-Zied, and T. H. Mansoure, “Effect of fuel/oxidizer ratio and the calcination temperature on the preparation of microporous-nanostructured tricobalt tetraoxide,” Advanced Powder Technology, vol. 25, no. 2, pp. 560–566, 2014.

M. T. Makhlouf, B. M. Abu-Zied, and T. H. Mansoure, “Direct fabrication of cobalt oxide nanoparticles employing sucrose as a combustion fuel,” Journal of Nanoparticles, vol. 2013, Article ID 384350, 7 pages, 2013.

D. Patil, P. Patil, V. Subramanian, P. A. Joy, and H. S. Potdar, “Highly sensitive and fast responding CO sensor based on Co₃O₄ nanorods,” Talanta, vol. 81, no. 1-2, pp. 37–43, 2010.

S. N. Basahel, I. H. A. El-Maksod, B. M. Abu-Zied, and M. Mokhtar, “Effect of Zr⁴⁺ doping on the stabilization of ZnCo-mixed oxide spinel system and its catalytic activity towards N₂O decomposition,” Journal of Alloys and Compounds, vol. 493, no. 1-2, pp. 630–635, 2010.

G. Maniak, P. Stelmachowski, A. Kotarba, Z. Sojka, V. Rico-Pérez, and A. Bueno-López, “Rationales for the selection of the best precursor for potassium doping of cobalt spinel based deN₂O catalyst,” Applied Catalysis B: Environmental, vol. 136-137, pp. 302–307, 2013.

G. Maniak, P. Stelmachowski, F. Zasada, W. Piskorz, A. Kotarba, and Z. Sojka, “Guidelines for optimization of catalytic activity of 3d transition metal oxide catalysts in N₂O decomposition by potassium promotion,” Catalysis Today, vol. 176, no. 1, pp. 369–372, 2011.

B. M. Abu-Zied, “Oxygen evolution over Ag/FexAl2−xO₃ catalysts via N₂O and H₂O₂ decomposition,” Applied Catalysis A: General, vol. 334, no. 1-2, pp. 234–242, 2008.

Ž. Chromčáková, L. Obalová, F. Kovanda et al., “Effect of precursor synthesis on catalytic activity of Co₃O₄ in N₂O decomposition,” Catalysis Today, vol. 257, no. 1, pp. 18–25, 2015.

T. Franken and R. Palkovits, “Investigation of potassium doped mixed spinels as catalysts for an efficient N₂O decomposition in real reaction conditions,” Applied Catalysis B: Environmental, vol. 176-177, pp. 298–305, 2015.