ZnO/ZnAl2O4 Nanocomposite Films Studied by X-Ray Diffraction, FTIR, and X-Ray Photoelectron Spectroscopy

ZnO/ZnAl 2 O 4 nanocomposite films were synthesised by ultrasonic spray pyrolysis (USP) by extracting Al 2 O(SO 4 ) 2 oxide with zinc chloride hydrate in deionised water. The sample was then subjected to heat treatment at 650C and 700C for 1 h, which led to the formation of the spinel oxide (ZnAl 2 O 4 ) and wurtzite (ZnO) phases. Al 2 (SO 4 ) 3 ⋅18H 2 O salt was transformed into aluminum oxide sulfate Al 2 O(SO 4 ) 2 , which is an intermediary decomposition product, by calcination at 795C for 3 h. The structures of the synthesised ZnO/ZnAl 2 O 4 films were confirmed by XRD, FTIR, and X-ray photoelectron spectroscopy (XPS). XPS spectra of the major Zn, Al, and O photoelectron lines and the major X-ray induced Zn LMM Auger lines for ZnO/ZnAl 2 O 4 are presented.


Introduction
Zinc aluminate (ZnAl 2 O 4 ) is of interest due to its desirable properties, such as its high mechanical resistance, high thermal stability, low-temperature sinterability, low surface acidity, and good diffusion [1].These characteristics make it very suitable for applications as a high-temperature material, catalyst, catalyst support, ceramic pigment, and optical and thermal control coating for spacecraft, and it is emerging as one of the best wide-band-gap compound semiconductors (  = 3.8 eV) for UV optoelectronic applications [2].In addition, ZnAl 2 O 4 is also widely used in many catalytic reactions, cracking, dehydration, hydrogenation, pollution control, and dehydrogenation [3,4].According to Hadnadev-Kostić et al., the calcination of ZnAl layered double hydroxides leads to the formation of high-photocatalytic-activity mixed ZnO-ZnAl 2 O 4 oxides with high surface area and thermal stability.This enhancement of the photocatalytic behaviour is due to the presence of the ZnO semiconductor (  = 3.2 eV), which has a photocatalytic potential assigned to its activation in the visible region and the presence of the spinel phase [5].
This letter is a contribution to the simplest preparation methods for mixed oxides.The ZnO/ZnAl 2 O 4 system has been successively prepared by a USP method employing Al 2 (SO 4 ) 3 ⋅18H 2 O salt as a new precursor for the ZnAl 2 O 4 phase.We also attempt to determine the appropriate synthesis conditions in terms of the substrate and annealing temperatures for the formation of composite films.This paper also presents the XPS spectra of the major Zn, Al, and O photoelectron lines and the major X-ray induced Zn LMM Auger lines for ZnO/ZnAl 2 O 4 .

Experimental
Aluminium sulphate hydrate salt was used as the Al metal source in our synthesis.For this purpose, different calcination temperatures in the range of 750 to 1200 ∘ C were applied to Al 2 (SO 4 ) 3 ⋅18H 2 O initial powder to induce its thermal decomposition.We have chosen to report the analysis of the 785 and 795 ∘ C treatments in this study.The calcination was carried out in air atmosphere for 3 h.The spraying solution was 0.06 M in zinc chloride dihydrate (ZnCl 2 ⋅2H 2 O) and 0.12 M in the calcination final product with distilled water as the solvent.This solution was maintained under constanttemperature (below 100 ∘ C) agitation for 8 h.Magnetic stirrer agitation promoted the chemical reaction between precursors, facilitating the dissolution of the salts in water and maintaining the high homogeneity of the solution.The ultrasonic spraying system used in this work consists of a commercial ultrasonic atomizer VCX 134 AT and a substrate holder with heater.The ultrasonic vibrator frequency was 40 kHz and the power used was 130 W. The median drop size at 40 kHz is 45 m.The nozzle-substrate distance was 5 cm and, during the deposition, the solution flow rate was held constant at 0.2 mL/min.The substrate (quartz) temperature (Ts) during deposition was 570 ∘ C, and the deposition time was fixed at 30 min.After deposition, the sample was annealed in air for 1 h at 650 ∘ C and 700 ∘ C.
The crystalline structure of the deposited specimen was determined by X-ray diffraction (XRD) with a radiation wavelength of 1.5418 Å (CuK  ).The chemical bonding states of the as-calcined powder or the films obtained were characterised by Fourier-transform infrared spectrometry (Nicolet 460 FTIR) at room temperature.The sample for FTIR measurements was prepared by grinding the film scraped from the quartz substrate.The uncertainty in the position of the various peaks is ±2 cm −1 .The thermogravimetric (TG) data were recorded under a dry air flow with a heating rate of 5 ∘ C/min in a SETARAM TGDTA92 16.18 thermal analyser.TG measurements were corrected for temperaturedependent buoyancy by subtracting the data of a measurement carried out on an inert sample.The X-ray photoelectron spectroscopy (XPS) analysis was carried out with a PHI 5000 VersaProbe-Scanning ESCA Microprobe using monochromatized Al K  X-ray source (ℎ] = 1486.6eV, 15 kV, 39.3 W, diameter beam spot: 200 m) by calibrating binding energy to C1s (285.1 eV).The surface contaminants were removed by means of mild sputtering method using 2 kV Ar + ions.

Results and Discussion
Figure 1(a) illustrates the FTIR patterns of the intermediate products of the 3-h calcination of the aluminium sulphate hydrate powder at 785 or 795 ∘ C. The spectra present some notable differences related to the molecular and structural bonding states of the calcined powder.Three bands are assigned to the ] 3 (SO 4 2− ) mode for the salt heated at 785 ∘ C: 1150, 1181, and 1250 cm −1 .The SO 4 2− group in sulphate minerals can exhibit four infrared-active vibrational modes, including a strong F antisymmetric bend (] 3 ) and a generally weak E symmetric bend (] 2 ).These vibrational bands generally occur as two to four ] 3 bands between 960 and 1280 cm −1 and one or two ] 2 bands between 420 and 525 cm −1 [7].The weaker ] 2 vibration band appears at approximately 500 cm −1 .It should be noted that the principal changes in the FTIR spectra are observed in the bands located between 584 and 712 cm −1 .Indeed, the FTIR curve of aluminium sulphate hydrate calcined at 785 ∘ C includes additional characteristic triplet absorption bands at 584-712 cm −1 compared to the spectrum of that calcined at 795 ∘ C.These bands can be attributed to vibrations of the (Al-O-Al) 4+ group [8].Additionally, the FTIR patterns of calcined powders exhibit a band at 3443 cm −1 and a weak band at 1638 cm −1 , which are assigned to the vibration mode of chemically bonded hydroxyl groups and the deformation vibration of water molecules, respectively.Three peaks of very weak intensities at 2856 cm −1 , 2927 cm −1 , and 2960 cm −1 are attributed to the C-H stretching vibrations of alkane groups [9].
The thermal decomposition of aluminium sulphate hydrate is a possible means for the production of high-purity aluminium oxides with fine grains via intermediate steps [10] Figure 1(b) shows the typical thermogravimetric (TG) curve and the first derivative of the weight loss (DTG) plot for Al 2 (SO 4 ) 3 ⋅18H 2 O salt.The TG curve and DTG plot are indicated as solid and dotted lines, respectively.The TG-DTG can be interpreted as follows: the aluminum sulfate hydrate decomposition takes place in several steps.The first three major steps are dehydration reactions in which eighteen moles of water is lost.In the range of 40-90 ∘ C, only a small weight loss is observed (about 6%).This is due to the fact that not all the water is released.As the temperature increases above 90 ∘ C, the coarse aluminum sulfate hydrate particles shatter, releasing water vapor.This is manifested by the fast weight loss on the TG curve of aluminum sulfate hydrate (≈24.5% between 90 and 151 ∘ C).Up to the end temperature of the third DTG peak (380 ∘ C), the cumulative weight loss of the sample was 46.5%, which approached the theoretical weight loss from the conversion of Al 2 (SO 4 ) 3 ⋅18H 2 O to Al 2 (SO 4 ) 3 (48.6%).The formation of aluminum sulfate occurs when the temperature was between 706 ∘ C and 785 ∘ C. The weight loss increased with increasing the treatment temperature and the formation of Al 2 O(SO 4 ) 2 is observed at temperatures between 785 ∘ C and 800 ∘ C (0.83 moles of SO 4 leaves the aluminum sulfate at 795 ∘ C).The theoretical weight loss due to the conversion of Al 2 (SO 4 ) 3 ⋅18H 2 O to Al 2 O(SO 4 ) 2 is 60.6%.The last major step includes the sulfate ions decomposition to sulfur oxide vapor.The DTG peak with maxima at ≈808 ∘ C (about 70.7% weight loss) of sample is due to -Al 2 O 3 phase formation.The loss of mass continued until approximately 900 ∘ C (about 84.7% weight loss), where -Al 2 O 3 is formed.
The XRD patterns of the final products of alum salt calcination at 785 and 795 ∘ C for 3 h are presented in Figure 2. The spectra relative to the powder obtained after calcination at 785 ∘ C show that it is polycrystalline.The diffraction peaks present in the XRD diffractogram are identical to those of the aluminium sulphate (Al 2 (SO 4 ) 3 ) reference pattern (JCPDS Card number 01-077-0066).When the calcination temperature was increased from 785 to 795 ∘ C (Figure 2), the intensity of the aluminium sulphate phase peaks decreased, and several disappeared.At 795 ∘ C, the XRD results, combined with the FTIR results, indicate that the aluminium sulphate phase was present but at a lower amount than at 785 ∘ C. The weak peak intensities of the substance produced at 795 ∘ C reveal that a large amount of it was poorly crystallised.Matori et al. have found that the Al 2 (SO 4 ) 3 phase lost its bonding and crystallinity after Al 2 (SO 4 ) 3 ⋅18H 2 O was calcined at 900 ∘ C [11].However, the persistence and shape of the XRD peak at the 2 = 44.07∘ position suggests that the nucleation of the -alumina phase had begun.The correlation between the XRD spectrum and the FTIR results obtained for the powder calcined at 795 ∘ C suggests that the Al 2 O(SO 4 ) 2 metastable phase of the chemical decomposition of aluminium sulphate hydrate exhibits the rhombohedral structure of the aluminium sulphate present at this temperature.
The structural characterisation of the deposited specimen by the simple ultrasonic spray pyrolysis technique using the white solid formed after calcining the initial Al 2 (SO 4 ) 3 ⋅18H 2 O precursor at 795 ∘ C for 3 h in the spraying solution and annealed at two different temperatures during 1 hour is reported in Figure 3 ((a) 700 ∘ C and (b) 650 ∘ C).The XRD diffractogram relative to the coating treated by a 700 ∘ C-1 h heat treatment (Figure 3(a)) reveals the coexistence of zinc oxide and zinc aluminate.All peaks are well defined, indicating the highly crystalline nature of the phases present in the sample.Every diffraction peak of all phases is in good agreement with the standard diffraction patterns of hexagonal ZnO and cubic ZnAl 2 O 4 spinel structures according to JCPDS card numbers 00-036-1451 and 00-001-1146, respectively.The lattice constants can be calculated using the following formulas: where  and  are the lattice constants and  ℎ is the crystalline surface distance for ℎ indices.With the data in Table 1, the lattice constants of the ZnO and ZnAl 2 O 4 films were calculated to be  =  = 3.248 Å,  = 5.208 Å and  Information on the crystallite size () for the films (i.e., ZnO/ZnAl 2 O 4 ) was obtained from the full width at half maximum of the diffraction peaks using the Scherrer formula: where , (ℎ), and (ℎ) are the X-ray wavelength (0.15418 nm), Bragg diffraction angle, and line width at half maximum, respectively.This formula is not limited by the preferential orientation and is valid for an ordinary XRD profile.To improve the statistics, the most intense peaks in the profiles were chosen to determine the crystallite size.
The average crystallite sizes of ZnO and ZnAl 2 O 4 were estimated to be 43 nm and 12 nm, respectively.
Rietveld refinement verified the formation of the ZnO/ZnAl 2 O 4 composite films after also an annealing at 650 ∘ C for 1 h and is reported in Figure 3(b).Excellent agreement is observed in terms of the peak positions and intensities between the theoretical and observed data, as depicted in Figure 3(b).The lattice parameters obtained from the Rietveld analysis of the ZnO and ZnAl 2 O 4 structures are  =  = 3.250 Å,  = 5.208 Å and 8.097 Å, respectively, and the reported values are  =  = 3.250 Å,  = 5.207 Å and 8.087 Å, respectively, according to the JCPDS data.This close agreement indicates the phase purity of the two oxides obtained.The average crystallite sizes of ZnO and ZnAl 2 O 4 were estimated to be 47 nm and 13 nm, respectively.
The relative crystallinity of each phase in the oxides mixture can be estimated by counting software diffractograms XRD (X'Pert HighScore).This estimation for the deposited system annealed at 650 ∘ C during 1 hour, for example, is of 60% for ZnO phase and 40% for ZnAl 2 O 4 one.
In accordance with the X-ray diffraction analysis of the spraying product, the FTIR results of the deposited specimen heat treated at 700 ∘ C during 1 h (see Figure 4) demonstrate the presence of ZnO/ZnAl 2 O 4 mixed compounds.The absorption peaks located at 675, 557, and 502 cm −1 are characteristic of the regular spinel structure with octahedrally coordinated aluminium centres only [12].The absorption peak located at 431 cm −1 , corresponding to the Zn-O vibration frequency, is clearly represented, which is in agreement with the results obtained by XRD, and is significant red shifted compared with that of bulk ZnO manufactured via the French process (437.33 cm −1 ) [13].
To probe with a fine way the present elements in our system as well as their chemical environment, the X-ray photoelectron spectroscopy (XPS) technique was employed.Indeed, the correlation of the different core levels binding energy positions with compounds properties which can be present in the film, the variations in binding energies, or chemical shifts of the photoelectron lines in the experimental curves reflect the modifications of the average atomic potential undergone by these electrons depending on the chemical bonds involved.This has been extremely useful in many studies.The sputtering of the sample surface in comparison with its initial surface induces changes in the binding displacement which refer directly to the preparation and preservation of the specimen.The film surface sputter cleaning step was inside the XPS chamber and XPS analyses were investigated both on the as-deposited and removable surface specimens.The XPS survey spectrum of the asdeposited coating (heat treated at 700 ∘ C for 1 h) reported in Figure 5 indicates the presence of Zn, O, and Al elements.However, some carbon and sulfur are incorporated in the as-deposited film and with more smaller quantities after a surface sputtering.
Figure 6(a) shows the XPS survey spectra of the asdeposited and sputter-cleaned (after 2 min, Ar + sputtering (∼2 nm)) films.The quantitative analysis indicates that the surface atomic composition percentages of Zn, Al, and O change from 15.3, 14.6, and 53.4 [14].An important factor regarding the surface property of oxides is the occurrence of preferential segregation of one ion over another on the surface leading to a difference between the bulk and surface composition and in turn on catalytic properties.The atomic ratio of elements Zn/Al of the asdeposited film is about 1.04 : 1 and that of 2 min sputtercleaned film is 0.91 : 1, deviating from the theoretical value of 1 : 1 calculated from the chemical formula of ZnO/ZnAl 2 O 4 .This result shows that the surface Zn/Al atomic composition is somewhat different from the bulk composition.
Figure 6(b) shows the XPS spectra in the Zn 2p region for these samples (as-deposited and sputter-cleaned thin film).The Zn 2p core level spectrum for thin film shows a doublet, whose binding energies are 1022.7 and 1045.9 eV (1022.0 and 1045.2 eV for the sputter-cleaned), which can be identified as the Zn 2p3/2 and Zn 2p1/2 lines, respectively.The binding energy differences between the two lines are 23.2 eV (23.2 eV for the sputter-cleaned), which is comfortably lying close to the standard reference value of ZnO [15].The Zn 2p3/2 and Zn 2p1/2 binding energy positions and binding energy difference, calculated from XPS analysis, reveal the oxidation of the Zn atoms to the Zn 2+ chemical state.Recorded to the Zn 2+ 2p doublet collected before the surface ionbombardment, a similar line shapes but a decrease in intensity and a minor shift in binding energy positions were detected, which indicates that the environment of Zn 2+ at the top surface is slightly different from Zn 2+ underneath it [16].
A high resolution XPS scan of the Al 2p peak reveals the nature of the aluminum bonding.Figure 6(c) shows the comparison of the Al 2p peaks for the sample before and after Ar + sputter cleaning for 2 min.The center of the peak shifts from 74.7 to 74.0 eV.The binding energy of the Al 2p signal is compatible with the presence of Al 3+ species.
Figure 6(d) shows the XPS spectra in the Al 2s region for these samples (as-deposited and sputter-cleaned thin film).There is no considerable shift in Al 2s binding energy value centered around 119.5 and 118.8 eV for the as-deposited and sputter-cleaned thin film, respectively, indicating the presence of Al 3+ on the surface.For the as-deposited film, no change in line shape was observed for Al 3+ except for a decrease in intensity and a minor shift in binding energy, which shows that the environment of Al 3+ at the top surface is slightly different from Al 3+ underneath it.The same trend was observed for Zn 3s peak at 140.3 eV and 140.0 eV for the as-deposited and thin film, respectively.
Kim et al. reported that when Al-doped ZnO epitaxial layer is prepared and analysed by XPS, the strong O 1s peak at 530.6 eV is a characteristic of O 2− ions on the wurtzite structure of a hexagonal Zn 2+ ion array, and the weak O 1s peak at 532.0 eV is characteristic of a nonstoichiometric Al-O phase [17].Chen et al., in an investigation of XPS and AES of Al-doped ZnO, reported that the three distinct components of O 1s can be attributed to the presence of loosely bound oxygen on the ZnO surface (532.4 eV), O 2− ions in the oxygen deficient regions within the ZnO (531.25 eV), and O 2− ions on the wurtzite structure of the hexagonal Zn 2+ ion array (530.15eV), respectively [18].The deconvolution of the XPS spectra of the O 1s spectrum is shown in Figure 6(e).The O 1s core level spectrum of as-deposited film seems to be asymmetrical and can be best fitted using two Gaussian curves at 531.28 (FWHM 2.7) and 531.97 (FWHM 3.69) and may be attributed to the oxygen of ZnO crystal lattice [19] and oxygen of ZnAl 2 O 4 [15], respectively.The O 1s core level spectrum of sputter-cleaned thin film can be best fitted using two Gaussian curves at 530.86 (FWHM 3.41) and 532.19 eV (FWHM 3.93).In case of sputter-cleaned film, the intensity at 532.2 eV binding energy decreases dramatically whereas the intensity of 532.19 eV peak increases.
Figure 6(f) shows the area of the survey scan in the proximity of the C 1s peak at 285.1 eV, S 2s, and S 2p regions of the (as-deposited and sputter-cleaned) coating annealed at 700 ∘ C for 1 h.A significant diminution in the intensity of the carbon line seen in the relative curve to the surface film after Ar + sputtering is characteristic of the purity of the bulk specimen from the carbon specie contamination.Tuan et al. explain this observation by the total reaction of the metal-organic precursor molecules and the desorbing of the carbon-containing ligands from the surface, so the peak in the as-deposited film spectrum is probably because the adventitious hydrocarbons apparently built up on the sample during the transfer through air [20].Some sulfur content is detected in the as-deposited thin film, which becomes negligible after sputter cleaning of the film.The low sulfur content of the deposited film is likely due to decomposition of the aluminum oxide sulfate (Al 2 O(SO 4 ) 2 ) precursor.
In this study, the modified Auger parameter method [15] (i.e., modified Auger parameter =   = binding energy of the major photoelectron line plus the kinetic energy of the major Auger line for the element of interest) was used to determine the chemical state of zinc.It is known that the   values located at 2010 and 2014 eV are characteristic of the oxidation state (Zn 2+ ) and metallic state (Zn 0 ), respectively [15].For as prepared and sputter-cleaned ZnO/ZnAl 2 O 4 films, the shifts of the   are given in Table 2.That the   values kept constant at ∼2010.2 eV, being far from 2014 eV, indicates the existence of Zn 2+ [21].The calculated modified Auger parameter values for zinc oxide and ZnO/ZnAl 2 O 4 system are identical but differed from the calculated value for the zinc aluminate by only 0.6 eV, as can be observed.This difference is usually not considered very pronounced and the differentiating between ZnO and ZnO/ZnAl 2 O 4 and/or ZnAl 2 O 4 becomes not possible and exhibits other data than   values alone.A similar approach (rend) and deduction were reported by Strohmeier et al. to distinguish between ZnO and Zn(OH) 2 and/or ZnAl 2 O 4 in their studied zincated disc, where the difference between the   values obtained for these compounds was 0.4 eV [22].However, the O ls values determined for the sputter-cleaned ZnO/ZnAl 2 O 4 system and ZnAl 2 O 4 material are equals and up to one electron volt in comparison with that of ZnO oxide.As can be seen from Table 2, the O 1s binding energy shows a chemical shift of 1.7 eV between ZnO/ZnAl 2 O 4 (as-deposited film) and ZnO.

Conclusion
In this study, a ZnO/ZnAl 2 O 4 system was successfully obtained from an inexpensive aluminium sulphate hydrate salt as the Al metal source by ultrasonic spray pyrolysis.The Al 2 (SO 4 ) 3 ⋅18H 2 O thermal decomposition product after calcination at 795 ∘ C for 3 h in air atmosphere combined with ZnCl 2 ⋅2H 2 O salt in distilled water constitutes an efficient

Figure 1 :
Figure 1: FTIR absorption spectrum of the calcination products (3 h, 785 or 795 ∘ C) of Al 2 (SO 4 ) 3 ⋅18H 2 O powder and that of Al 2 (SO 4 ) 3 ⋅18H 2 O powder for comparison (grey line) (the main bands are discussed in the text) (a) and thermogravimetric (TG) curve for Al 2 (SO 4 ) 3 ⋅18H 2 O at 5 ∘ C/min (b).The theoretical number of water molecules and weight loss associated with each Al 2 (SO 4 ) 3 unit are given.

Figure 2 :
Figure 2: XRD patterns of the final products of alum salt calcination at 785 and 795 ∘ C for 3 h.
. Alumoxane cations (Al 2 O 4+ ) from aluminum oxide sulfate Al 2 O(SO 4 ) 2 and sulphite ions (SO 3 2− ) are present in the intermediate products formed during the thermal decomposition of Al 2

Table 1 displays
XRD data of ZnO/ZnAl 2 O 4 films.It shows typical polycrystalline hexagonal ZnO structures.The (002) peak has the highest intensity.Characteristics of ZnAl 2 O 4 were also presented.
at % to 16.5, 18.0, and 57.3 at %, respectively, after sputter cleaning the surface.These results are in good consistence with the expected theoretical values of Zn, Al, and O of the ZnAl 2 O 4 and ZnO compounds, included in the general concentrations, assumed to other Figure 4: FTIR absorption spectrum of the ZnO/ZnAl 2 O 4deposited USP system and heat treated at 700 ∘ C for 1 h.Figure 5: XPS survey spectrum of the as-deposited ZnO/ZnAl 2 O 4 film annealed at 700 ∘ C for 1 h.negligible oxygen configurations like the C-O contaminant one.The observed quantitative at.% concentrations of the Zn, Al, and O principal elements are in good agreement with the XRD analysis, where we have demonstrated the formation of a cubic crystalline phase of the ZnAl 2 O 4 and wurtzite ZnO phase

Table 2 :
XPS binding energies (eV) for zinc reference compounds and ZnO/ZnAl 2 O 4 system (annealed at 700 ∘ C). a As-deposited film, b surface cleaned film, and Auger values in kinetic energy (KE).Zinc Auger parameter = binding energy Zn 2p3/2 + kinetic energy Zn LMM.spraying solution.A relatively low substrate temperature (570 ∘ C) for the ZnAl 2 O 4 formation was employed.The preparation conditions permit the formation of a nanometric ZnAl 2 O 4 phase.The structures of the synthesised ZnO/ZnAl 2 O 4 films were confirmed by XRD, FTIR, and Xray photoelectron spectroscopy.XPS spectra of the major Zn, Al, and O photoelectron lines and the major X-ray induced Zn LMM Auger lines for ZnO/ZnAl 2 O 4 are presented.