A comprehensive corrosion investigation of pure Fe in an environment of solid sodium salt deposit (i.e., NaCl or Na2SO4) with mixtures of H2O and O2 at 500°C was conducted by mass gain measurement, X-ray diffraction (XRD), scanning electron microscope (SEM), potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS). The results showed that corrosion rates were accelerated with solid NaCl or Na2SO4 deposit due to their reaction with the formed protective scale of Fe2O3 and subsequently resulted in its breakdown. The corrosion rate of pure Fe with solid NaCl is higher than that with solid Na2SO4 because of the lower activation energy (Ea) for chemical reaction of Fe in solid NaCl+H2O+O2 (i.e., 140.5 kJ/mol) than that in solid Na2SO4+H2O+O2 (i.e., 200.9 kJ/mol). Notably, the electrochemical corrosion rate of pure Fe with solid NaCl deposit, 1.16×10−4A/cm2, was a little lower than that with solid Na2SO4 deposit.
National Natural Science Foundation of China51671198513711811. Introduction
Corrosion of metal materials is severe in the environment with solid salt deposit and dry or wet O2 at medium and high temperatures [1–18], especially for turbine blades in planes or ships and power boilers. Due to their excellent mechanical properties, low cost, and ease of machining, pure Fe and its alloys are the popular materials that were investigated in solid alkali chloride deposit in dry or wet O2 [1–7]. Most researchers [2, 5, 6] thought that the solid NaCl could react with Fe2O3 to generate Cl2 via the reaction, 2NaCl+Fe2O3+1/2O2=Na2Fe2O4+Cl2. Then, Cl2 could react with Fe to form FeCl(s), i.e., Cl2+Fe=FeCl2s. As such, FeCl2(s) would continuously evaporate under low vapor pressure at high temperature. The FeCl2 vapor would diffuse outward through cracks and pores of the scale. Finally, the FeCl2 vapor would react with O2 to form Fe3O4 and/or Fe2O3 when they met during the process. Apparently, the solid NaCl could react with the oxidation scale that formed in dry or wet air at medium and high temperatures and lead to the breakdown of the protective scale to accelerate the corrosion rate of materials. Folkenson et al. [7] proposed a new mechanism as follows. Solid KCl reacts with O2 and H2O to generate chloride ions (i.e., 2KCl+1/2O2+H2O+2e−⟶2KOHads+2Cl−ads) and subsequently react with iron ions to form FeCl2(s). Cao et al. [3] postulated a hypothesis of “dynamic water film” in which H2O molecules were continuously being absorbed on and evaporated from the surface of the material. The electrochemical corrosion might occur in the dynamic water film, which accelerates the corrosion of metal [3]. Shu et al. [10] used impedance spectroscopy to investigate the corrosion mechanisms of pure Fe and pure Cr with solid NaCl deposit in water vapor at 600°C. According to the analysis of the resistance and capacitance of corrosion scale, the electrochemical corrosion was proved to occur in the corrosion environments. After that, Tang et al. [1] investigated the interaction between chemical reactions and electrochemical reactions of pure Fe in this corrosion environment. The chemical reactions and electrochemical reactions follow “ce mechanism,” in which Fe and Fe2O3 first react chemically with NaCl, water vapor, and oxygen to generate HCl (g). Then, the HCl (g) reacts with pure Fe electrochemically via a one-electron electrochemical reduction to form H2.
Compared to the alkali chlorides, the corrosion mechanisms of metal/alloys with solid sulfate are lacking. However, the corrosion mechanisms are focused on molten sulfate. Recently, many studies have been carried out on the corrosion behavior of metals/alloys in a molten Na2SO4 environment [19–25] and many corrosion mechanisms have been proposed. One of the well-known mechanisms is the sulfidation model [19, 20], in which the formation of sulfides accelerates the corrosion. The other one is the acidic-basic fluxing [19, 21–24] mechanism, in which dissolution of the protective oxide scales, due to formation of basic Na2O, was considered the reason for the accelerated corrosion. Moreover, based on the electrochemical mechanism [25], corrosion was considered an electrochemical reaction in which the transfer of electrons accelerated the corrosion. Tang et al. [26] investigated the corrosion behavior of pure Fe under solid Na2SO4 deposit in wet oxygen flow at 500°C. The results showed that the corrosion of Fe includes chemical corrosion and electrochemical corrosion. The chemical reaction and electrochemical reaction follows the “ce mechanism.” Fe and Fe2O3 first react chemically with Na2SO4, water vapor, and oxygen to generate H2SO4 (g). And then, the H2SO4 (g) reacts with pure Fe electrochemically via a one-electron electrochemical reduction to form H2. The coeffect between deposited solid Na2SO4 and H2O+O2 certainly exists and significantly accelerates the corrosion of pure Fe.
NaCl and Na2SO4 are normal corrosive mediums. The corrosion of materials in solid salt environment depends on the anion of the salt [18, 27]. However, the effects of the different solid deposits (NaCl and Na2SO4) on the corrosion behavior of pure Fe in water vapor are still unclear. In this paper, the corrosion differences of pure Fe with solid NaCl and solid Na2SO4 deposit in water vapor were comparatively studied to cognize the corrosion behaviors of materials in the corrosion profoundly.
2. Experimental
The pure Fe (99.9%) was used as experimental specimen. The metallography of the specimen is shown in Figure 1. The microstructure of pure Fe is ferrite. The maximum grain size is about 100 μm. Before the experiment, the sample was ground using silicon-carbide abrasive papers down to 1000 grit, degreased in acetone then ethanol, and dried in air before use. The NaCl and Na2SO4 are of analytical purity (≥99.5%). The solid salt was deposited on the preheated Fe sample surface by repeatedly brushing and drying a salt-saturated solution. The mass of salt was about 4 mg/cm2. The temperature of the furnace was controlled at 500°C. H2O came from an 80°C water bath. Pure O2 was passed through the glass bubbler with a flux of 200 ml/min.
Metallograph of pure Fe.
The corrosion test was carried out in a thermal balance [2]. To prevent the H2O from condensing in the upper part of the thermal balance, a counterflow of N2 was passed through the apparatus at 150 ml/min. After the furnace was heated to the desired temperature and the gas flow was stabilized, the specimen was quickly suspended into the furnace tube, and the test was started. All the measurements were carried out at ambient pressure. After the tests, the specimens were further examined by XRD and SEM.
A special three-electrode system was built for the electrochemical measurements in this particular environment [1]. To decrease the resistance of the solution and obtain a uniform electric field, the reference electrodes consisted of four platinum wires, each with a diameter 0.4 mm, and the counter electrode was a circular strip of platinum foil about 2 mm wide. All potential values in this paper were reported versus this platinum reference electrode. The Fe working electrode was a rod 10 mm long and 5 mm diameter. The three electrodes were placed in quartz tubes, which acted as insulators. All the gaps were sealed by high-temperature inorganic glue. The three-electrode system after solid NaCl and solid Na2SO4 deposition was directly put into the furnace at the desired temperature and with water vapor for electrochemical measurements.
A PAR2273 Electrochemical Measurement System manufactured by EG&G was used for all electrochemical measurements, which also has the function to compensate the resistance between reference electrode and working electrode. In the galvanic corrosion measurement, the ratio of anodic area to cathodic area is 1 : 2. In the potentiodynamic polarization measurements, the measurements were carried out after 1000 s in the corrosion environment for obtaining an electrochemical stability and the scan rate was 1 mV/s. The resistance between reference and working electrodes was compensated during measurements according to the design of electrochemical system and testing work station. All measurements were repeated more than three times.
3. Results and Discussion
Figure 2 shows the mass gain of pure Fe as a function of time at 500°C with and without solid NaCl or Na2SO4 [26] in O2 containing water vapor. As is seen from Figure 2, the corrosion of pure Fe is accelerated with solid NaCl or Na2SO4 deposit. Compared to the case with solid Na2SO4 deposit, the corrosion rate of pure Fe with solid NaCl deposit is slightly higher at all-time duration.
Mass gain plots of pure Fe with and without solid NaCl or Na2SO4 deposit in O2 containing water vapor at 500°C.
In our previous studies [1, 13], it is found that the corrosion of pure Fe in both corrosion environments includes a chemical corrosion process and an electrochemical corrosion process, while the overall corrosion is dominated by the chemical corrosion process with a percentage of over 90%. Herein, we investigated the differences of chemical corrosion that is influenced by NaCl and Na2SO4.
To affect the chemical corrosion rate, there are two aspects: (a) the protection of scale on the surface of pure Fe. The compact and integrated scale can restrain the corrosion of substrate. (b) The activity of corrosion reactants. As it is known, the corrosion rate would increase with a decreasing active energy. The details of the effects are discussed as follows.
The scale includes solid salt deposition scale (NaCl or Na2SO4) and corrosion scale on the surface of pure Fe. Figures 3(a) and 3(b) show the surface morphologies of solid NaCl and Na2SO4, respectively, before corrosion test. The results showed that both salt scales are loose and porous. However, the solid NaCl film was much looser and more porous than solid Na2SO4 film, which led to an easy transport of H2O and O2 to the interface of pure Fe and solid NaCl film, promoting the chemical corrosion process of pure Fe.
Surface morphologies of solid salt scale on pure Fe before experiment: (a) solid NaCl; (b) solid Na2SO4.
The corrosion of materials with solid salt deposit in water vapor is different with that in aqueous solution. The corrosion scale would stay on the surface of substrate, which should restrain the corrosion of substrate. Figure 4 shows the cross-sectional morphologies of pure Fe after 10 h corrosion at 500°C in NaCl+H2O+O2 (Figure 4(a)) and Na2SO4+H2O+O2 (Figure 4(b)) [26]. It indicated that the corrosion scale formed on the surface of pure Fe was loose and porous in both corrosion environments. A number of volatile species are formed in the corrosion process, which could contribute to the formation of the loose and porous corrosion scale [6]. As a matter of fact, some green deposits were observed on the tube inner surface of the furnace after many hours of experiments, confirming the formation of volatile species. However, the scale formed in solid NaCl+H2O+O2 is looser and higher porosity than that formed in solid Na2SO4+H2O+O2 [26]. This indicated that the reactants (H2O and O2) could be easier to transport through the corrosion scale formed in the environment with NaCl. Eventually, it promotes the chemical corrosion process of pure Fe.
Cross-sectional morphologies of pure Fe with NaCl or Na2SO4 deposit in O2 flow with water vapor for 10 h: (a) solid NaCl and (b) solid Na2SO4.
The components of the corrosion scale formed on the surface of pure Fe in solid NaCl+H2O+O2 or Na2SO4+H2O+O2 [26] after 10 h corrosion are shown in Figure 5. The components of the scales in the two corrosion environments are remarkably different. The component of the scale on the surface of pure Fe formed in solid NaCl+H2O+O2 is hematite that mainly consists of Fe2O3, while the component of the scale on the surface of pure Fe formed in solid Na2SO4+H2O+O2 mainly consists of Fe3O4 with a little of Fe2O3. According to the published research [27], the generation of Fe2O3 or Fe3O4 is closely relative to oxygen pressure. Fe2O3 would be generated at a relatively high oxygen pressure, while Fe3O4 would be generated at a relatively low oxygen pressure. From Figures 3 and 4, the NaCl scale is looser with higher porosity than Na2SO4 scale; meanwhile, the corrosion scale formed in the case of NaCl+H2O+O2 was also looser with higher porosity than that formed in the case of Na2SO4+H2O+O2. The oxygen could transport inward through the corrosion scale and solid NaCl scale easily. The oxygen pressure in the corrosion scale that formed in NaCl+H2O+O2 is higher than that formed in Na2SO4+H2O+O2. This is the reason why the components of the corrosion scales in the two corrosion environments were different.
XRD results of the corrosion scale of pure Fe in water vapor with solid NaCl or Na2SO4 deposits at 500°C.
The corrosion mechanism of pure Fe in the two corrosion environments could be understood on the basis of the components, morphologies of the corrosion scales, and published research.
For the case of solid NaCl, firstly, NaCl reacts with Fe2O3 and H2O to generate Na2Fe2O4 and HCl [4].
(1)2NaCls+Fe2O3+H2O=Na2Fe2O4+HCl.
The generated HCl could react with Fe to form FeCl2 [4], meanwhile, HCl could also react with O2 to form Cl2 [27].
(2)2HCl+Fe=FeCl2s+H24HCl+O2=2Cl2+2H2O
The Cl2 could react with Fe to form FeCl2 [28].
(3)Fe+Cl2=FeCl2s
The vapor pressure for FeCl2(s) is 4×10−5Pa at 500°C. A continuous evaporation will take place [6].
(4)FeCl2s=FeCl2g
The FeCl2(g) diffuse outward through the scale and react with O2 and H2O to form a loose and porous Fe2O3 scale (see Figure 4(a)) [4].
(5)2FeCl2+1/2O2+2H2O=Fe2O3+4HCl
For the case of solid Na2SO4, firstly, Na2SO4 reacts with Fe2O3 and H2O to generate Na2Fe2O4 and H2SO4 [26].
(6)Na2SO4+Fe2O3+H2O=Na2Fe2O4+H2SO4
The generated H2SO4 could react with Fe to form FeSO4.
(7)H2SO4+Fe=FeSO4+H2
According to the XRD results, the FeSO4 could react with O2 and H2O to form Fe3O4 and Fe2O3.
(8)5FeSO4+5H2O+O2=Fe3O4+Fe2O3+5H2SO4
The generation of H2SO4 and H2 led to the formation of many holes and cracks in the scale (see Figure 4(b)).
According to the morphologies shown in Figures 3 and 4, the more porous NaCl scale and corrosion scale formed in the NaCl+H2O+O2 promoted the chemical corrosion process. However, this did not fully explain why the corrosion rate of pure Fe in NaCl+H2O+O2 was higher than that in Na2SO4+H2O+O2. The activation energy is a key parameter to estimate the chemical reaction rate. The lower the activation energy, the more atoms, ions, or molecules of substances are activated to transition state. Therefore, the rate of chemical reaction increases with decreases in chemical reaction activation energy.
Both corrosion mechanisms of pure Fe in solid NaCl+H2O+O2 and solid Na2SO4+H2O+O2 corrosion environments follow the ce mechanism [1, 26]. For the ce mechanism, the relationship between phase angle and frequency could be given as Equation (9) [28].
(9)cotϕ=2ω1/2/λ+1/1+ei1/1+K1+g21/2+g/1+g21/2+K/1+K+ei1/1+ei1/1+K1+g21/2−g/1+g21/2+K/1+K+ei,(10)g=k1+k2ω,(11)λ=khfD1/2e−αj+eβj,(12)K=k1k2,(13)β=1−α,(14)j=nFRTEd.c.−E1/2r,where Φ is used for representing for phase angle, k1 and k2 for chemical reaction rate constants, ω for angular frequency, D for diffusion coefficient, kh for apparent heterogeneous rate constant, f for activity coefficient, α for charge transfer coefficient, n for number of electrons transferred, Ed.c. for applied d. c. potential, E1/2r for reversible half-wave potential, and F, R, and T for their conventional electrochemical meanings. The value of k1 can be calculated using Equation (9). Figure 6 shows the relationship between frequency and phase angles of pure Fe in solid NaCl+H2O+O2 at 500°C. The plots have a maximum. It suggests that the corrosion mechanism of pure Fe in the two corrosion environments involves the interaction of the chemical and the electrochemical reactions, which is similar with pure Fe in solid Na2SO4+H2O+O2 [26]. The calculated values of k1 for pure Fe in solid NaCl+H2O+O2 and solid Na2SO4+H2O+O2 corrosion environments are 0.230 sec-1 and 0.031 sec-1, respectively. Therefore, the chemical corrosion rate of pure Fe in solidNaCl+H2O+O2 is higher than that in solid Na2SO4+H2O+O2 because of its higher chemical reaction rate constant in the case with solid NaCl.
Frequency dependence of the phase angle of Fe in water vapor with NaCl or Na2SO4 deposits at 500°C at open circuit potential.
Chemical reaction rate is closely related with the activation energy. The lower the activation energy is, the higher the chemical reaction rate is. According to the logarithmic Arrhenius equation, the rate constant (k) dependence of temperature (T) is given by the relationship (g) [29]:
(15)lnk=lnA−EaRT,where k is used for representing for the rate constant, A for a temperature-independent constant (often called the frequency factor), T for the absolute temperature, R for the universal gas constant, and Ea for the activation energy. According to Equation (15), a plot of lnk vs. 1/T gives a straight line with slope of -Ea/R. The values of Ea for Fe in solid Na2SO4+H2O+O2 corrosion environments can be obtained from the slope of Figures 7. The value is 200.9 kJ/mol. The value of Ea for Fe in solid NaCl+H2O+O2 corrosion environments is 140.5 kJ/mol [13]. The lower activation energy of Fe in solid NaCl+H2O+O2 accounts for its higher chemical reaction and the higher overall corrosion rate.
Temperature dependence of chemical reaction rate constant of pure Fe with solid Na2SO4 deposit in O2 flow with water vapor.
The electrochemical corrosion of pure Fe in solid Na2SO4+H2O+O2 corrosion environments has been shown in our earlier studies [1, 26]. The potentiodynamic polarization plot of pure Fe in solid NaCl+H2O+O2 at 500°C is shown in Figure 8. The anodic current densities of pure Fe in both two corrosion environments increase linearly with anodic potential increasing in the active polarization zone, which can be attributed to active dissolution in the aqueous environment, because the loose and porous corrosion scale could not inhibit the electrochemical corrosion. The cathodic reaction rate of pure Fe in solid Na2SO+H2O+O2 is higher than that in NaCl+H2O+O2. The electrochemical corrosion rates (icorr) were calculated by fitting the potentiodynamic polarization curves in the active polarization zones. The electrochemical corrosion current density (icorr) obtained was 1.16×10−4A/cm2 and 1.30×10−4A/cm2 for pure Fe in solid NaCl+H2O+O2 and solid Na2SO4+H2O+O2 [26], respectively. The amount of Fe corroded by electrochemical reaction was obtained using Faraday’s rule. After the calculation, the chemical reaction rates of pure Fe in the two corrosion environments within 1 h are 0.036 g/h/cm2 and 0.041 g/h/cm2, respectively. It must illustrate that the calculation time herein is in one hour, because the potentiodynamic polarization measurements were carried out within one hour, and there is no significantly variety of the electrochemical corrosion rate in one hour. This was proved by presented authors used an electrochemical instrument named CMB 1510B (based on weak polarization theory) manufactured by State Key Laboratory for Corrosion and Protection, to measure the electrochemical corrosion rate every 4 minutes during the whole corrosion reaction. The electrochemical corrosion rate of pure Fe in solid NaCl+H2O+O2 is slightly lower than that in solid Na2SO4+H2O+O2.
Potentiodynamic polarization plots of pure Fe in water vapor with solid NaCl or Na2SO4 deposits at 500°C.
As is well-known, charge transfer is the fundamental characteristic of the electrochemical reaction [30, 31]. The corrosion scale and solid salt scale are the key influence factors for electrochemical reaction rate. The corrosion scale of pure Fe formed in solid NaCl+H2O+O2 is looser and more porous than those formed in solid Na2SO4+H2O+O2 (see Figure 4), and the solid NaCl scale is also looser and more porous than solid Na2SO4 scale (see Figure 3). The HCl could volatilize and diffuse through the looser and more porous corrosion scale and NaCl scale easily. Thus, the cathodic reaction rate of pure Fe in solid Na2SO4+H2O+O2 is higher than that in solid NaCl+H2O+O2. As a consequence, the electrochemical corrosion rate of pure Fe in solid Na2SO4+H2O+O2 is higher than that in solid NaCl+H2O+O2.
As a consequence, the electrochemical corrosion rate of pure Fe in solid Na2SO4+H2O+O2 is higher than that of it in solid NaCl+H2O+O2. In addition, the components of the corrosion scales formed on the surface of pure Fe in solid NaCl+H2O+O2 and solid Na2SO4+H2O+O2 after 10 h corrosion are shown in Figure 5. The component of the scales on the surface of pure Fe formed in solid NaCl+H2O+O2 is hematite that mainly consists of Fe2O3, while the component of the scales on the surface of pure Fe formed in solid Na2SO4+H2O+O2 is Magnetite that mainly consists of Fe3O4. The protection of Fe2O3 is well than that of Fe3O4 [32], which also inhibit the electrochemical corrosion rate of pure Fe in solid NaCl+H2O+O2 corrosion environment.
4. Conclusion
The corrosion rate of the pure Fe is significantly accelerated under a NaCl or Na2SO4 deposit in an atmosphere of H2O+O2 at 500°C. Both the salts of NaCl and Na2SO4 could react with Fe2O3 to result in a breakdown of the protective scale and subsequently accelerate the corrosion rate of pure Fe.
Compared to the case in solid Na2SO4+H2O+O2, the corrosion rate of pure Fe is much higher in solid NaCl+H2O+O2. The activation energy (Ea) for chemical reaction of pure Fe in solid Na2SO4+H2O+O2 is 200.9 kJ/mol, which is higher than that of pure Fe in solid NaCl+H2O+O2.
The percentage contribution of the electrochemical reactions in total corrosion is insignificant. It was also found that the electrochemical corrosion rate of pure Fe with solid NaCl deposit was 1.16×10−4A/cm2, which was a little lower than that with solid Na2SO4 deposit.
Data Availability
The data used to support the findings of this study are available from the corresponding author upon request.
Conflicts of Interest
The authors declare that they have no conflicts of interest.
Acknowledgments
This work was supported by the National Natural Science Fund of China under the contract No. 51371181 and No. 51671198.
TangY. B.LiuL.LiY.WangF. H.Evidence for the occurrence of electrochemical reactions and their interaction with chemical reactions during the corrosion of pure Fe with solid NaCl deposit in water vapor at 600 °C201012219119310.1016/j.elecom.2009.11.0212-s2.0-74149087177ShuY. H.WangF. H.WuW. T.Synergistic Effect of NaCl and Water Vapor on the Corrosion of 1Cr-11Ni-2W-2Mo-V Steel at 500-700°C1999511/29711010.1023/A:1018854202982CaoM.LiuL.YuZ. F.FanL.YingL.WangF. H.Studies on the corrosion behavior of Fe-20Cr alloy in NaCl solution spray at 600 °C201813316517710.1016/j.corsci.2018.01.0332-s2.0-85041108006WangF. H.ShuY. H.Influence of Cr content on the corrosion of Fe-Cr alloys: the synergistic effect of NaCl and water vapor2003593/420121410.1023/A:10230833090412-s2.0-0038510002LiuL.LiY.ZengC. L.WangF. H.Electrochemical impedance spectroscopy (EIS) studies of the corrosion of pure Fe and Cr at 600 °C under solid NaCl deposit in H2O200651224736474310.1016/j.electacta.2006.01.0332-s2.0-33646587698GrabkeH. J.ReeseE.SpiegelM.The effects of chlorides, hydrogen chloride, and sulfur dioxide in the oxidation of steels below deposits19953771023104310.1016/0010-938X(95)00011-82-s2.0-0029328934FolkesonN.JonssonT.HalvarssonM.JohanssonL. G.SvenssonJ. E.The influence of small amounts of KCl(s) on the high temperature corrosion of a Fe-2.25Cr-1Mo steel at 400 and 500°C201162760661510.1002/maco.2010059422-s2.0-79955536219ShuY. H.WangF. H.WuW. T.Corrosion behavior of Ti60 alloy coated with a solid NaCl deposit in O2 plus water vapor at 500–700 °C1999525/646347310.1023/A:1018864216554FanL.LiuL.YuZ. F.CaoM.LiY.WangF. H.Corrosion behavior of Ti60 alloy under a solid NaCl deposit in wet oxygen flow at 600 °C20166111210.1038/srep290192-s2.0-84977068187ShuY. H.WangF. H.WuW. T.Corrosion behavior of pure Cr with a solid NaCl deposit in O2 plus water vapor2000545/645747110.1023/A:10046905182252-s2.0-0034505827WangF. H.GengS. J.ZhuS. L.Corrosion behavior of a sputtered K38G nanocrystalline coating with a solid NaCl deposit in wet oxygen at 600 to 700 oC2002581/218519510.1023/A:10160727263382-s2.0-0012780617WangC.JiangF.WangF. H.Corrosion inhibition of 304 stainless steel by nano-sized Ti/silicone coatings in an environment containing NaCl and water vapor at 400–600°C2004621/211310.1023/B:OXID.0000038782.77162.5b2-s2.0-4344613571TangY. B.LiuL.LiY.WangF. H.The electrochemical corrosion mechanisms of pure Cr with NaCl deposit in water vapor at 600 oC20111588C237C24110.1149/1.35961672-s2.0-80051730976FanL.LiuL.CaoM.YuZ.LiY.ChenM.WangF.Corrosion behavior of pure Ti under a solid NaCl deposit in a wet oxygen flow at 600 °C201664728210.3390/met60400722-s2.0-84961673925FanL.LiuL.CuiY.CaoM.YuZ. F.OguzieE. E.LiY.WangF. H.Effect of streaming water vapor on the corrosion behavior of Ti60 alloy under a solid NaCl deposit in water vapor at 600 degrees C2019160, article 10817716517810.1016/j.corsci.2019.1081772-s2.0-85072769373ReeseE.GrabkeH. J.Einfluß von Natriumchlorid auf die oxidation von hochlegierten Chrom- und Chrom-Nickel-Stählen1993442414710.1002/maco.199304402042-s2.0-84975886454KofstadP.1998London, BritishElsevier Applied ScienceShinataY.NishiY.NaCl-induced accelerated oxidation of chromium1986263-420121210.1007/BF006591842-s2.0-0022790216RappR. A.Whitney Award Lecture—1986:Chemistry and electrochemistry of the hot corrosion of metals1986421056857710.5006/1.3583026SimonsE. L.BrowningG. V.LiebhafskyH. A.Sodium sulfate in gas turbines19551112172610.5006/0010-9312-11.12.17BornsteinN. S.DecrescenteM. A.The role of sodium and sulfur in the accelerated oxidation phenomena-sulfidation197026730931410.5006/0010-9312-26.7.309BornsteinN. S.DecrescenteM. A.The role of sodium in the accelerated oxidation phenomenon termed sulfidation19712102875288310.1007/BF028132662-s2.0-0015143906GoebelJ. A.PettitF. S.The influence of sulfides on the oxidation behavior of nickel-base alloys19701123421342910.1007/BF030378742-s2.0-33749284491GoebelJ. A.PettitF. S.Na2SO4-induced accelerated oxidation (hot corrosion) of nickel1970171943195410.1007/BF02642794LiM.2001Beijing, ChinaMetallurgical Industry PressTangY. B.LiuL.FanL.LiY.WangF. H.The corrosion behavior of pure iron under solid Na2SO4 deposit in wet oxygen flow at 500 °C2014796144615710.3390/ma70961442-s2.0-8490687562928788182ZahsA.SpiegelM.GrabkeH. J.Chloridation and oxidation of iron, chromium, nickel and their alloys in chloridizing and oxidizing at mospheres at 400-700oC20004261093112210.1016/S0010-938X(99)00142-02-s2.0-0034059031SmithD. E.Alternating current polarography of electrode processes wih coupled homogeneous chemical Reactions. I. Theory for systems with first-order preceding, following, and catalytic chemical reactions196335660260910.1021/ac60199a0342-s2.0-0000394619ChenL. Z.ZhangY. H.2005ShanghaiShanghai Science and TechnologyQiaoY. X.XuD. K.WangS.MaY. J.ChenJ.WangY.ZhouH.Effect of hydrogen charging on microstructural evolution and corrosion behavior of Ti-4Al-2V-1Mo-1Fe alloy20216016817610.1016/j.jmst.2020.06.010QiaoY. X.TianZ. H.CaiX.ChenJ.WangY. X.SongQ. N.LiH. B.Cavitation erosion behaviors of a nickel-free high-nitrogen stainless steel20196711910.1007/s11249-018-1118-72-s2.0-85056765718GleitzerC.Electrical properties of anhydrous iron Oxides1996125-12635541810.4028/www.scientific.net/KEM.125-126.355