The Scientific World Journal

Volume 2014 (2014), Article ID 326427, 6 pages

http://dx.doi.org/10.1155/2014/326427

Research Article

Mechanistic Features of Nanodiamonds in the Lapping of Magnetic Heads

Xionghua Jiang,¹ Zhenxing Chen,¹ Joy Wolfram,² and Zhizhou Yang³

¹School of Chemistry and Chemical Engineering, Sun Yat-sen University, Guangzhou 510275, China

²National Center for Nanoscience & Technology of China, Beijing 100190, China

³Department of Emergency, Jinling Hospital Medical School of Nanjing University, Nanjing 210000, China

Received 27 February 2014; Revised 9 May 2014; Accepted 19 May 2014; Published 22 June 2014

Academic Editor: Erjia Liu

Copyright © 2014 Xionghua Jiang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

Nanodiamonds, which are the main components of slurry in the precision lapping process of magnetic heads, play an important role in surface quality. This paper studies the mechanistic features of nanodiamond embedment into a Sn plate in the lapping process. This is the first study to develop mathematical models for nanodiamond embedment. Such models can predict the optimum parameters for particle embedment. From the modeling calculations, the embedded pressure satisfies and the indentation depth satisfies . Calculation results reveal that the largest embedded pressure is 731.48 GPa and the critical indentation depth is 7 nm. Atomic force microscopy (AFM), scanning electron microscopy (SEM), and Auger electron spectroscopy (AES) were used to carry out surface quality detection and analysis of the disk head. Both the formation of black spots on the surface and the removal rate have an important correlation with the size of nanodiamonds. The results demonstrate that an improved removal rate (21 nm·min⁻¹) can be obtained with 100 nm diamonds embedded in the plate.

1. Introduction

Nanodiamonds refer to diamonds with a diameter equal to or less than 100 nm. These particles not only exhibit properties of diamonds, but also have special nanoparticle characteristics, such as small size, unique surface properties, and macroscopic quantum tunneling [1, 2]. In recent years, many scholars have performed research on the stability, shape, and particle size distribution of nanodiamonds [3, 4]. Nanodiamonds aggregate easily, so studies on dispersion of nanodiamonds are especially important. In particular, recent studies have focused on the thermodynamic, dynamic, and aggregate stability of nanodiamonds [5–8]. Many scholars have performed valuable research on the dispersion of nanodiamonds in aqueous systems [9–12]. However, because of the metallic properties of magnetic head materials, the lapping process requires nonaqueous systems to avoid potential chemical corrosion. Dispersion of nanodiamonds in nonaqueous systems directly affects the stability of the particles embedded in the plate, thus affecting the surface lapping quality of the magnetic head. Solid content, oil density, and surface modifying agents of nanodiamonds are considered to be the main factors affecting the dispersion in nonaqueous systems [13, 14]. Due to hard aggregation composed of Van Edward forces and hydrogen bonds and soft aggregation caused by the surface atomic binding force, the methods to improve nanodiamond stability include the following: (i) adding a surfactant that effects surface absorption or chemical reactions of nanodiamonds, (ii) using polymer nanodiamond powder instead of a monomer to avoid particles getting in close proximity to each other, and (iii) ultrasonic dispersion [15–17]. When nanodiamonds with good dispersion are used, the slurry is harder, has higher heat transfer and endurance, and improves chemical stability [18–21]. When nanodiamonds are used in the lapping of magnetic heads, the surface roughness can be greatly reduced [22–25]. Some scholars believe that the mechanism of improvement is due to the existing ball bearing effect between the spherical nanodiamond and the Sn plate, where rolling and gliding friction coexist. The nanodiamonds can significantly increase lapping endurance and reduce the friction effect [26, 27]. Other researchers believe that the improved performance is due to the existing boundary lubrication among the nanodiamonds, the magnetic heads, and the oil, all of which greatly reduce friction [28]. There are few studies on the process of nanodiamond embedment into a Sn plate in the lapping process. In this paper, the mechanistic features of nanodiamond embedment are analyzed and for the first time mathematical formulas are established to model this process. These models encompass two key factors: the pressure of nanodiamonds embedded into the plate and the embedment depth. These parameters impact the lapping surface of the magnetic head, especially the formation of black spots and the material removal rate. Therefore, the models can be used to calculate optimum depth and pressure values for the embedment process.

As can be seen in Figures 1 and 2, scanning electron microscopy (SEM) and atomic force microscopy (AFM) images reveal black spots on the surface of magnetic heads. Black spots refer to round areas with white reflection that are usually bigger than 10 nm in diameter and have diamond-like protrusions. Since the capacity of a Sn plate to hold nanodiamonds is limited, the pressure and embedment depth of nanodiamonds are very important. When the nanodiamonds are exposed to less pressure, the embedment depth is shallow, and the number of embedded particles is less. In this case, it is hard for the magnetic head materials to touch the diamonds in the lapping process. The nanodiamonds embedded into the plate surface can also easily fall off and flow along with the slurry. In both cases, this will cause a low removal rate. When the nanodiamonds are under more pressure, the embedded depth will be deeper and the amount of embedded particles will increase, resulting in deformation of the Sn plate and defects in the head surface, including scratches, protrusions, recession, and black holes. Auger electron spectroscopy (AES) E1127-08 was used to do further research on the composition of the black spots, as shown in Table 1. The experimental data confirmed that the carbon content of the region with black spots is much higher than that of a normal region.

Table 1: Auger electron spectroscopy (AES) data for black spots.

Composition
Black spots
Normal shield area

C
43.60%
18.90%

Ni
44.70%
64.10%

Fe
11.70%
16.90%

Figure 1: (a) Scanning electron microscopy (SEM) images of black spots, obtained with Hitachi S4800 high resolution SEM with Vacc 2.0 kV, ×40 K. (b) Atomic force microscopy (AFM) images of the corresponding black spots from the SEM images, obtained with PSIA AFM from PARK Company, Korea, using tapping mode and a scan size of  μm.

Figure 2: 3D AFM images detected of the protrusion (6.966 nm) and recession (4.458 nm) of black spots, obtained with PSIA AFM from PARK Company, Korea, using tapping mode and a scan size of 2 μm.

2. Establishment of a Model for Nanodiamond Embedment

2.1. Pressure Analysis

In the first step of the model, the effect of a single diamond was considered. A spherical diamond with a diameter of 100 nm was employed without movement or lubrication. The embedment was accomplished in two steps, as shown in Figure 3. The process evolved from elastic deformation to elastic-plastic deformation to plastic deformation and finally reached maximum plastic deformation. When the tough circle radius is the same as the diamond radius, the diamond is embedded into the shield.

Figure 3: Modeling of the embedment of a single nanodiamond.

Three values should be obtained for the model: (i) maximum elastic deformation (ii), maximum plastic deformation, and (iii) corresponding pressure. In the first step, plastic deformation takes place and maximum deformation appears when half of the diamond is embedded into the shield. Based on the classical plastic contact equation and considering adherent energy [29], we obtain

where refers to load, to adherent energy, to diamond radius, to tough circle radius, and to hardness. can be obtained from

where and refer to the surface force of shield and diamond, respectively, and refers to the related constant. When we regard as the radius of circle in the case of maximum deformation [30], we get

where refers to the pressure when plastic deformation begins.

In the second step, whole embedment takes place, based on classical contact mechanics theory [31]:

where  GPa,  GPa, , and ; thus  GPa. For a spherical diamond, and for plane; thus , and the largest pressure [32] is

2.2. Indentation Depth Analysis

As shown in Figure 4, according to the test method of microhardness, the indentation depth is determined by hardness and load as follows [33]:

Figure 4: Modeling of the indentation depth of a single nanodiamond.

From the above formula, we have , where is a constant related to the shape of the diamond.

2.3. Removal Rate Analysis

2.3.1. Plastic Deformation [34]

where is removal volume, is pressure, is hardness of removed materials, is sliding distance, and is a universal parameter determined by the friction coefficient, the diamond shape, plate charging quality, toughness, and plastic models of the magnetic heads.

2.3.2. Crack Deformation [34]

where is pressure, is hardness, is crack toughness, is sliding distance, and is a universal parameter determined by the shape and radius of the diamond.

3. Experiments

3.1. Material Preparation

Three types of nanodiamonds extracted from CKK slurry with different radii, which were used for head lapping plate preparation, were imaged with a Hitachi S4800 high resolution SEM, with Vacc 5.0 kV (Figure 5).

(a)

(b)

(c)

Figure 5: SEM pictures of diamonds. (a) 50 nm diamonds from 1/20, CKK Co., USA (×50 K). (b) 70 nm diamonds from 1/15, CKK Co., USA. (×50 K). (c) 100 nm diamond from 1/10, CKK Co., USA. (×50 K).

3.2. Machine and Embedding Process

A HYPREZ lapping machine from Engis Company, Japan, was used. As shown in Figure 6, the Sn plate and the fixture were rotated with different motors through transmission belts to keep the lapping speed adjustable. Freeze water was used to ensure constant temperature by removing heat. The plate and the ring were rotated at a fixed speed in the same direction. A magnetic bar (PMR, produced by TDK Co.) was fixed on the ring with rubber. Each magnetic bar had 81 heads (sliders) and a size of  mm. Slurry was added from a capillary tube and subjected to continuous stirring.

Figure 6: Lapping machine.

The base material of the plate was Sn. The rotation speed was set at 30 rpm·min¹. The ring rotation speed was set at 25 rpm·min⁻¹, the weight was 6 kg, and the shaving time was 25 min. The lubrication was AM-ZX-60 from Engis Co. Removal rates were measured by calculating the resistance of magnetic heads before and after lapping by using a SSCL-F precision magnetic test machine made by TDK, Japan.

3.3. Results and Discussion

3.3.1. Pressure and Indentation Depth

The magnetic head is composed of an AlTiC hard and brittle ceramic substrate with several micrometer thick metal read and write pole tips ( mm). The substrate is composed of 64% Al₂O₃ and 36% TiC (volume ratio), achieved by sintering. The mechanical properties are shown in Table 2. The composite ceramic of AlTiC has a large density, with a hardness of 23.7 GPa, which is higher than that of the pure ceramic Al₂O₃ (about 19 GPa). Therefore, the addition of TiC can improve the mechanical performance of the magnetic head substrate.

Table 2: Mechanistic properties of magnetic head materials.

Material
HV (GPa)
(GPa)
(MPa·m1/2)

64% Al₂O₃ 

36% TiC
23.7
390
3.77

From (5), it can be calculated that the largest pressure put on the nanodiamonds is 731.48 GPa and the critical indentation depth is 7 nm. Namely, when the indentation depth is less than 7 nm, plastic deformation occurs, while crack deformation takes place at depth of more than 7 nm.

In the lapping process, the average diameter of the nanodiamonds was approximately 100 nm. And the particle size distribution of nanodiamonds, as shown in Figure 7, was tested by HORIBA LB-550 granulometer. The measured data showed that the scope of these three types of diameter distribution was almost the same, from 50 nm to 240 nm, except the principal distribution difference. The diamonds were suspended in slurry, which was mixed as the magnetic bar and plate rotated. The magnetic bar was pressed onto the plate with a loading plate and a pressing block. Under the shear force from the relative motion between the grinding plate and the magnetic bar, some of the diamonds became embedded into the plate. When a diamond is pressed into the plate and reaches a certain depth, the plate exerts an elastic deformation force on the diamonds that is much larger than the magnetic shear stress from the magnetic bar. Consequently, the diamonds are fixed onto the grinding plate, forming a cutting edge. Microcutting of the magnetic surface occurs due to the relative motion between the lapping plate and the magnetic bar, thereby obtaining a smooth machined surface. However, nanodiamonds are typically embedded onto the plate using random pressure, and the sizes of the diamonds usually differ, causing various indentation depths. This in turn causes variations in the magnetic bar surface cutting height, which can lead to the formation of microscratches. Therefore, the establishment of mathematical models, such as (5) and (6), that can predict the indentation depth of diamonds is necessary to avoid microscratches [35].

(a) 50 nm

(b) 67 nm

(c) 100 nm

Figure 7: Particle size distribution of nanodiamonds. (a) 50 nm diamonds from 1/20, CKK Co., USA. (b) 70 nm diamonds from 1/15, CKK Co., USA. (c) 100 nm diamond from 1/10, CKK Co., USA.

3.3.2. Removal Rates

Equations (7) and (8) demonstrate that the removal volume will increase if the pressure () and sliding distance () are increased. The removal rate increases as the weight increases. When the plate speed is raised, in unit lapping time increases, leading to an increase in removal rate. When these parameters are fixed, removal rates are primarily determined by the diameter of the nanodiamonds. In this experiment, nanodiamonds with three different diameters were used (100 nm, 75 nm, and 50 nm). The original data of the removal rates of magnetic heads in the lapping process is about 20 nm·min⁻¹. As can be seen in Table 3, higher removal rates are obtained as the diameter of the nanodiamonds increases, thereby showing that the experimental result correlates with the model predictions. The removal rate is 21 nm·min⁻¹ when 100 nm nanodiamonds were used in lapping process, which was higher than the other two types of diamonds.

Table 3: Comparison of removal rates of nanodiamonds with different diameters.

Nanodiamonds
Diameter (nm)
Removal rate (nm·min⁻¹)

 CKK
50
1.2

 CKK
75
6.966

 CKK
100
21

4. Summary

A mechanistic model of nanodiamonds embedded into a Sn plate has been established in this paper. The pressure satisfies . And the indentation depth satisfies . The calculations reveal that the largest embedded pressure is 731.48 GPa, and the critical indentation depth is 7 nm. A removal rate equation has also been established. The removal rate equation under plastic deformation satisfies and under crack deformation satisfies . In conclusion, the lapping process can be predicted and the surface quality of magnetic heads can be improved by using these formulas.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgment

This work is supported by the Lapping Laboratory of SAE Technologies (Dongguan) Co., Ltd.

References

A. A. Gromov, S. A. Vorozhtsov, V. F. Komarov, G. V. Sakovich, Y. I. Pautova, and M. Offermann, “Ageing of nanodiamond powder: physical characterization of the material,” Materials Letters, vol. 91, pp. 198–201, 2013.

E. Osawa, Handbook of Advanced Ceramics, 2nd edition, 2013.

J. Mona, J.-S. Tu, T.-Y. Kang, C.-Y. Tsai, E. Perevedentseva, and C.-L. Cheng, “Surface modification of nanodiamond: photoluminescence and Raman studies,” Diamond and Related Materials, vol. 24, pp. 134–138, 2012.

H. D. Wang, Q. Yang, H. Niu, and I. Badea, “Adsorption of azo dye onto nanodiamond surface,” Diamond and Related Materials, vol. 26, pp. 1–6, 2012.

E. Osawa, “Recent progress and perspectives in single-digit nanodiamond,” ,Diamond and Related Materials, vol. 16, no. 12, pp. 2018–2022, 2007.

X. Z. Liu, T. Yu, Q. P. Wei, Z. M. Yu, and X. Y. Xu, “Enhanced diamond nucleation on copper substrates by employing an electrostatic self-assembly seeding process with modified nanodiamond particles,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 412, pp. 82–89, 2012.

Q. Zou, Y. G. Li, L. H. Zou, and M. Z. Wang, “Characterization of structures and surface states of the nanodiamond synthesized by detonation,” Materials Characterization, vol. 60, no. 11, pp. 1257–1262, 2009.

I. Neitzel, V. Mochalin, I. Knoke, G. R. Palmese, and Y. Gogotsi, “Mechanical properties of epoxy composites with high contents of nanodiamond,” Composites Science and Technology, vol. 71, no. 5, pp. 710–716, 2011.

Sumaiya, I. Raafat, and N. Ibrahim, “Mechanism of abrasive wear in nanomachining,” Tribology Letters, vol. 42, pp. 275–284, 2011.

G. M. Schmid, M. Miller, and C. Brooks, “Step and flash imprint lithography for manufacturing patterned media,” Journal of Vacuum Science and Technology B: Microelectronics and Nanometer Structures, vol. 27, no. 2, pp. 573–580, 2009.

R. P. Ambekar, D. B. Bogy, Q. Dai, and B. Marchon, “Critical clearance and lubricant instability at the head-disk interface of a disk drive,” Applied Physics Letters, vol. 92, no. 3, Article ID 033104, 2008.

D. Kim, W. T. Kim, H. M. Kim, H. Chen, P. Jain, and M. S. Jhon, “A novel simulation of air/liquid bearings based on lattice Boltzmann method,” Journal of Applied Physics, vol. 105, no. 7, Article ID 07B701, 2009.

S. Zhang, B. Strom, S. C. Lee, and G. Tyndall, “Simulating the air bearing pressure and flying height in a humid environment,” Journal of Tribology, vol. 130, Article ID 011008, 4 pages, 2008.

N. Liu and D. B. Bogy, “Boundary effect on particle motion in the head disk interface,” Tribology Letters, vol. 33, no. 1, pp. 21–27, 2009.

S. K. Deoras and F. E. Talke, “Effect of intermolecular forces on the dynamic response of a slider,” Journal of Tribology, vol. 129, no. 1, pp. 177–180, 2007.

N. Tagawa, A. Mori, and K. Senoue, “Effects of molecularly thin liquid lubricant films on slider hysteresis behavior in hard disk drives,” Journal of Tribology, vol. 129, no. 3, pp. 579–585, 2007.

B. Tomcik, T. Osipowicz, and J. Y. Lee, “Diamond-like film as a corrosion protective layer on the hard disk,” Thin Solid Films, vol. 360, no. 1-2, pp. 173–180, 2000.

K. Takata, “Strain imaging of a magnetic layer formed on an air bearing surface of a hard disk drive head for perpendicular recording,” Journal of Vacuum Science and Technology B: Microelectronics and Nanometer Structures, vol. 27, no. 2, pp. 997–1000, 2009.

S. Weissner, Numerical and experimental investigation of the load/unload behavior of subambient pressure hard disk drive sliders [Ph.D. thesis], University of California, Berkerly, Calif, USA, 2001.

S. J. Yoon, S. H. Son, and D. H. Choi, “Head slider designs considering dynamic L/UL systems for 1-in disk drives,” IEEE Transactions on Magnetics, vol. 44, 1, pp. 151–156.

T. R. Albrecht and F. Sai, “Load/Unload technology for disk drives,” IEEE Transactions on Magnetics, vol. 35, no. 2, pp. 857–862, 1999.

M. A. Dufresne and A. K. Menon, “Ultra-low flying height air bearing designs,” IEEE Transactions on Magnetics, vol. 36, no. 5, pp. 2733–2735, 2000.

S. Yonemura, S. Weissner, L. Zhou, and F. E. Talke, “Investigation of disk damage caused during load/unload using a surface reflectance analyzer,” Tribology International, vol. 38, no. 2, pp. 81–87, 2005.

Y. Hu, P. M. Jones, and K. Li, “Air bearing dynamics of sub-ambient pressure sliders during dynamic unload,” Journal of Tribology, vol. 121, no. 3, pp. 553–559, 1999.

S. Wang, F. P. Crimi, and R. J. Blanco, “Dynamic behavior of magnetic head sliders and carbon wear in a rampload process,” Microsystem Technologies, vol. 9, no. 4, pp. 266–270, 2003.

J. P. Peng, “Theoretical prediction of ramp loading/unloading process in hard disk drives,” Journal of Tribology, vol. 121, no. 3, pp. 568–574, 1999.

J. Luo, D. Shu, and B. Shi, “The pulse width effect on the shock response of the hard disk drive,” International Journal of Impact Engineering, vol. 34, no. 8, pp. 1342–1349, 2007.

S. Kumar, V. D. Khanna, and M. Sri-Jayantha, “Study of the head disk interface shock failure mechanism,” IEEE Transactions on Magnetics, vol. 30, no. 6, pp. 4155–4157, 1994.

A. Majumdar and B. Bhushan, “Fractal model of elastic-plastic contact between rough surfaces,” Journal of Tribology, vol. 113, no. 1, pp. 1–11, 1991.

D. O. Ouma, Modeling of Chemical Mechanical Polishing for Dielectric Planarization, MIT Department of Electrical Engineering and Computer Science, 1999.

K. L. Johnson, Contact Mechanics, Cambridge University Press, 1985.

Y. Xie and B. Bhushan, “Effects of particle size, polishing pad and contact pressure in free abrasive polishing,” Wear, vol. 200, no. 1-2, pp. 281–295, 1996.

J. F. Luo and D. A. Dornfeld, “Material removal mechanism in chemical mechanical polishing: theory and modeling,” IEEE Transactions Semiconductor Manufacturing, vol. 14, no. 2, pp. 112–133, 2011.

W. T. Tseng and Y. L. Wang, “Re-examination of pressure and speed dependences of removal rate during chemical-mechanical polishing processes,” Journal of the Electrochemical Society, vol. 144, pp. 15–17, 1997.

M. C. Pohl and D. A. Griffiths, “The importance of particle size to the performance of abrasive particles in the CMP process,” Journal of Electronic Materials, vol. 25, no. 10, pp. 1612–1616, 1996.